混凝土劣化的检测与修复
详细信息 本馆镜像全文    |  推荐本文 | | 获取馆网全文
摘要
介绍了混凝土劣化检测和修复的方法,研究表明:钢筋锈蚀、冻融循环、碱骨料反应和酸碱侵蚀是造成混凝土劣化的四个主要原因;现代化技术能够准确检测混凝土裂缝和钢筋锈蚀等劣化问题,主要非破损检测方法有:打击法、超声法、放射法、红外分析、瑞利波频谱、雷达和抗渗性检测等;混凝土劣化的修复要针对其劣化的原因来开展,主要有钢筋锈蚀修复、裂缝修复、剥落或蜂窝麻面修复、渗漏修复、补强几个方面。
The method to detect and repair the concrete deterioration was introduced. Studies showed that steel corrosion,freeze- thaw cycles, alkali aggregate reaction and acid erosion were the four main cause of concrete deteriorations. Modern technology can accurately detect the deterioration problem,such as cracking of concrete and rebar corrosion,etc. The non- destructive test methods are hitting method,ultrasonic method,radiation method,infrared analysis,rayleigh wave frequency spectrum, radar and permeability resistance test, etc. The repair of concrete deterioration can be conducted according to the deterioration cause,mainly include rebar corrosion repair,crack repair,flake or honeycomb pitting surface repair,leakage repair and reinforcement,etc.
引文
[1]卢汝生,吴秋飞.混凝土——人类的伟大发明[J].中山大学学报论丛,2001(1):296-299.
    [2]龚洛书,柳春圃.混凝土的耐久性及其防护修补[M].北京:中国建筑工业出版社,1990:1-5.
    [3]侯宝隆,蒋之峰编译.混凝土的非破损检测[M].北京:地震出版社,1992:1-379.
    [4]朱锦章,罗昕,赵霄龙.超声回弹法评定冻融混凝土的抗压强度[J].低温建筑技术,2005(3):3-5.
    [5]曲华,宁建国,李学慧.利用瑞利波频谱分析法无损检测混凝土结构[J].混凝土,2006(2):76-80.
    [6]张新华.准确检测混凝土抗渗性能的思考[J].混凝土,2003(5):15-17.
    [7]樊云昌,曹兴国,陈怀荣.混凝土中钢筋腐蚀的防护与修复[M].北京:中国铁道出版社,2001:195-209.
    [8]朱元光,张翠琴.混凝土的胶接、密封与修补[M].北京:中国铁道出版社,1994:130-139.

版权所有:© 2023 中国地质图书馆 中国地质调查局地学文献中心