高温后FRP筋纵向拉伸性能
详细信息 本馆镜像全文    |  推荐本文 | | 获取馆网全文
摘要
通过拉伸试验研究了高温后纤维增强聚合物(FRP)筋的纵向拉伸性能.试验参数包括温度、FRP筋直径、FRP筋种类和恒温时间.结果表明:室温下和高温后FRP筋拉伸应力-应变关系曲线相似;随着温度升高,FRP筋抗拉强度和极限应变逐渐下降;在试验温度范围内,高温作用对FRP筋的拉伸弹性模量影响较小;随着玄武岩纤维增强聚合物(BFRP)筋直径减小,高温作用后BFRP筋抗拉强度降低程度呈增加趋势;BFRP筋直径对弹性模量和极限应变的影响没有明显规律;高温作用对玻璃纤维增强聚合物(GFRP)筋的影响大于BFRP筋;270℃时FRP筋在0.5h前已完成大部分玻化、热分解反应.建议了300℃以内高温后FRP筋抗拉强度折减系数应取的值,当温度高于300℃时,BFRP筋和GFRP筋均不应使用.
Through tensile tests,longitudinal tensile properties of fiber reinforced polymer(FRP)bars after high temperature were studied.Test parameters include temperature,FRP bar diameter,FRP bar type and constant temperature time.The results show that,the stress-strain relationship curves before and after high temperature are similar.The tensile strength and ultimate strain of FRP bars decline gradually as temperature rises.Within the range of test temperature,tensile modulus of elasticity is less affected by high temperature.With the decrease of FRP bars diameter,the tensile strength reduction ratio of BFRP bars appears to increase.The diameter of BFRP bars has no obvious influence on modulus of elasticity and ultimate strain.The high temperature resistance of BFRP bars is better than that of GFRP bars.When the temperature is at 270 ℃,FRP bars have finished most glass transition and thermal decomposition in the first half an hour.Finally,tensile strength reduction factor of FRP bars after high temperature was suggested to be under 300°C,when the temperature is higher than 300 ℃,BFRP bars and GFRP bars should not be used.
引文
[1]郭恒宁.FRP筋与混凝土粘结锚固性能的试验研究和理论分析[D].南京:东南大学,2006.GUO Hengning.Experimental study and theoretical analysis on bond anchorage properties between FRP tendons and concrete[D].Nanjing:Southeast University,2006.(in Chinese)
    [2]高皖扬,胡克旭,陆洲导.火灾下碳纤维加固混凝土梁温度场分析[J].武汉理工大学学报,2008,30(11):129-135.GAO Wanyang,HU Kexu,LU Zhoudao.Temperature distribution analysis of carbon fiber strengthened concrete beams in fire[J].Journal of Wuhan University of Technology,2008,30(11):129-135.(in Chinese)
    [4]张云峰,张玉亮,詹界东,等.FRP筋长期耐腐蚀性能的研究与发展[J].低温建筑技术,2010(11):28-30.ZHANG Yunfeng,ZHANG Yuliang,ZHAN Jiedong,et al.Research and development of the long-term corrosion resistant performance of FRP tendons[J].Low Temperature Architecture Technology,2010(11):28-30.(in Chinese)
    [5]吴敬宇.玄武岩纤维复合筋高温性能研究[D].北京:中国地震局工程力学研究所,2011.WU Jingyu.Study on high temperature performance of basalt fiber reinforced polymer bars[D].Beijing:Engineering Mechanics Institute of China Earthquake Administration,2011.(in Chinese)
    [6]BISBY L A,KODUR V K R.Fire performance of FRP systems for infrastructure[R].Ottawa:National Research Council,2005.
    [7]MANAV M O.Mechanical properties of fiber reinforced polymer(FRP)composites for concrete bridge deck reinforcement[D].Florida:Florida Atlantic University,2002.
    [8]李士会.玻璃纤维聚合物筋及其与混凝土的粘结性能[D].郑州:郑州大学,2008.LI Shihui.Glass fiber reinforced polymer rebar and bond behaviors of GFRP rebar with concrete[D].Zhengzhou:Zhengzhou University,2008.(in Chinese)
    [9]周长东.GFRP筋增强混凝土结构抗火性能研究[D].上海:同济大学,2005.ZHOU Changdong.Fire resistance behavior of GFRP reinforced concrete structures[D].Shanghai:Tongji University,2005.(in Chinese)

版权所有:© 2023 中国地质图书馆 中国地质调查局地学文献中心