Q345B母材及其焊接接头的低周疲劳行为
详细信息 本馆镜像全文    |  推荐本文 | | 获取馆网全文
摘要
对Q345B及其光滑焊接接头的低周疲劳行为进行了试验研究。采用轴向对称应变控制方法,保持恒定应变速率为0.005 s-1,在0.3%~0.7%的应变范围内,在电液伺服疲劳试验机上测定了Q345B及其光滑焊接接头的低周循环应力响应特征、应变-寿命、应变-能量关系,并进行了对比分析。结果显示,Q345B母材在应变幅度低于和高于0.4%时分别呈现明显的循环软化和硬化现象,而焊接接头出现显著的硬化现象。与母材相比,焊接接头的低周转变寿命、疲劳强度和疲劳寿命明显减小。通过试验数据确定了Q345母材及其焊接接头Coffin-Manson关系的合理参数,建立了应变幅度-疲劳寿命及能量-寿命关系式。力学不均匀性引起的循环硬化趋势增加是导致焊接接头低周疲劳性能减低的主要原因。
Low cycle fatigue behaviors of Q345 B steel and smooth welded joint were experimentally investigated. The tests were carried out on a servo-hydraulic machine under fully reversed strain-control at constant strain rate of 0. 005 s- 1. The cyclic stress response characteristics,strain-life and strain-energy relationships of both base metal and welded joint were obtained and analyzed in the strain regime of 0. 3% ~ 0. 7%. The results showed that Q345 B showed significant cyclic hardening or softening respectively when the strain amplitudes were larger or lower than 0. 4%,while welded joint showed obvious cyclic hardening. The low cycle conversion life,fatigue strength and fatigue life of welded joint significantly decreased. The test data were used to derive suitable Coffin-Manson parameters and the strain-life,energy-life relationships were further determined. The increase of cyclic hardening caused by mechanical inhomogeneity was the main reason to the weakening low cycle fatigue properties of welded joint.
引文
[1]霍立兴.焊接结构的断裂行为及评定[M].北京:机械工业出版社,2000.
    [2]Cheng Guangxu.The investigation of low-cycle fatigue life for pressure vessel by damage mechanics approach[J].Journal of Xi’an Jiaotong University,1994,28(8):59-64.[程光旭.压力容器低周疲劳寿命的损伤力学理论研究[J].西安交通大学学报,1994,28(8):59-64.]
    [3]Puchi-Cabrera E S,Saya-Gamboa R A,La Barbera-Sosa J G,et al.Fatigue life of AISI 316L stainless steel welded joints,obtained by GMAW[J].Welding International,2009,23(10):778-788.
    [4]Luo Y,Huang C,Tian R,et al.Effects of strain rate on low cycle fatigue behaviors of high-strength structural steel[J].International Journal of Iron and Steel Research,2013,20(7):50-56.
    [5]Luo Yunrong,Wang Qingyuan,Liu Yongjie,et al.Low cycle fatigue properties of steel structure materials Q235 and Q345[J].Journal of Sichuan University:Engineering Science Edition,2012,44(2):169-175.[罗云蓉,王清远,刘永杰,等.Q235,Q345钢结构材料的低周疲劳性能[J].四川大学学报:工程科学版,2012,44(2):169-175.]
    [6]Gong Shihong,Sheng Guangmin,Li Yi,et al.Low cycle fatigeu property of pressure vessel steel 16MnR under earthquake load[J].Iron and Steel,1995,30(10):48-52.[龚士弘,盛光敏,李毅,等.压力容器钢16MnR在地震载荷下的低周疲劳性能[J].钢铁,1995,30(10):48-52.]
    [7]Yan X.Low cycle fatigue and cyclic stress ratcheting failure behavior of carbon steel 45 under uniaxial cyclic loading[J].International Journal of Fatigue,2005,27(9):1124-1132.
    [8]Pu Yumei,Wu Lin,Wu Jiecai.The overall anti seismic properties of Q235B and Q345BH H-beams[J].Anhui Metalurgy,2005(4):1-5.[蒲玉梅,吴林,吴结才.Q235B,Q345BH型钢综合抗震性能试验研究[J].安徽冶金,2005(4):1-5.]
    [9]Miao C,Zheng J,Gao X,et al.Investigation of low-cycle fatigue behavior of austenitic stainless steel for cold-stretched pressure vessels[J].Journal of Zhejiang University:Science A,2013,14(1):31-37.
    [10]Nip K H,Gardner L,Davies C M,et al.Extremely low cycle fatigue tests on structural carbon steel and stainless steel[J].Journal of Constructional Steel Research,2010,66(1):96-110.
    [11]Fricke W.Fatigue analysis of welded joints:State of development[J].Marine Structures,2003,16(3):185-200.
    [12]Teng T L,Fung C P,Chang P H.Effect of weld geometry and residual stresses on fatigue in butt-welded joints[J].International Journal of Pressure Vessels and Piping,2002,79(7):467-482.
    [13]Jaureguizahar L F,Chapetti M D.Estimating the fatigue behaviour of welded joints[C].The 12th Internerational Conference on Fracture.Ottawa:2013.
    [14]中国国家标准化委员会.GB/T15248—2008金属材料轴向等幅低循环疲劳试验方法[S].2008.
    [15]Nip K H,Gardner L,Davies C M,et al.Extremely low cycle fatigue tests on structural carbon steel and stainless steel[J].Journal of Constructional Steel Research,2010,66(1):96-110.
    [16]Song Fengming,Wen Donghui,Li Chen,et al.Low cycle fatigue characteristic of ultra-low yield point steel[J].Journal of Iron and Steel Research,2010,22(5):37-40.[宋凤明,温东辉,李陈,等.极低屈服点钢低周疲劳特性[J].钢铁研究学报,2010,22(5):37-40.]
    [17]Min Jie,Sheng Guangming,Wu Jiecai,et al.Analysis of high strain low cycle fatigue properties of hot rolled H beam steel[J].Journey of Iron and Steel Research,2009,21(11):41-44.[闵杰,盛光敏,吴结才,等.热轧H型钢的高应变低周疲劳性能研究[J].钢铁研究学报,2009,21(11):40-44.]
    [18]Coffin L F,Jr.A study of the effects of cyclic thermal stresses on a ductile metal[J].Transactions of ASME,1954,76(1):931-950.
    [19]Manson S S.Behavior of materials under conditions of thermal stress[R].Washington D C:National Advisory Committee for Aeroautics,TN 2933,1954.
    [20]Callaghan M D,Humphries S R,Law M,et al.Energybased approach for the evaluation of low cycle fatigue behaviour of 2.25 Cr-1Mo steel at elevated temperature[J].Materials Science and Engineering:A,2010,527(21):5619-5623.

版权所有:© 2023 中国地质图书馆 中国地质调查局地学文献中心