混凝土裂缝修复的断裂试验研究
详细信息 本馆镜像全文    |  推荐本文 | | 获取馆网全文
摘要
采用楔入劈拉法对比了有机材料环氧树脂与无机材料氯氧镁水泥浆两种材料修复混凝土裂缝的有效性。先对混凝土试件进行楔入劈拉试验,获得混凝土的断裂参数,然后采用环氧树脂灌缝胶、氯氧镁水泥浆对试件进行修复,再进行第二次楔入劈拉试验,测定注胶修复后的试件的相应断裂参数,并与初始混凝土试件的相应值进行对比分析,以此来考察并评估环氧树脂、氯氧镁水泥浆与混凝土粘结界面的性能以及两者的修复效果。试验结果表明:试件经过环氧树脂加固后,起裂断裂韧度与失稳断裂韧度得到不同幅度的提高,而氯氧镁水泥浆修复试件则有所下降。说明环氧树脂有效修复裂缝,抑制裂缝的重新开展,达到修复混凝土的效果;而采用氯氧镁水泥浆材料的修复效果没有环氧树脂修复效果好,为工程实际应用提供一些参考。
Based on the wedge-splitting tests of concrete specimens repaired with epoxy and MOC,the fracture energy,double-K fracture parameters and destroyed mode of prototype specimens and repaired specimens are analyzed and contrasted.The results of the experiments indicate that the fracture capability and carrying capacity of the repaired specimens are remarkably improved which show that epoxy injection is an adequate method for repairing cracked concrete.Instead,the test values of fracture parameters from concrete specimens repaired by MOC are decreased.The results can be provided for references of the engineering application of epoxy and MOC in repairing concrete.
引文
[1]清华大学土木工程结构专家组,西南交通大学土木工程结构专家组,北京交通大学土木工程结构专家组.汶川地震建筑震害分析[J].建筑结构学报,2008,29(4):1-9.Civil and Structural Groups of Tsinghua University,Xinan Jiaotong University and Beijing Jiaotong University.Analysis on seismic damage of buildings in the Wenchuan earthquake[J].Journal of Building Structures,2008,29(4):1-9.(in Chinese)
    [2]黄建锋,朱春明,龚治国,等.增大截面法加固震损钢筋混凝土框架的抗震性能试验研究[J].土木工程学报,2012,45(12):9-17.Huang Jianfeng,Zhu Chunming,Gong Zhiguo et al.Experimental study on seismic behavior of earthquake-damaged RC frame strengthened by enlarging cross-section[J].China Civil Engineering Journal,2012,45(12):9-17.(in Chinese)
    [3]殷杰,朱春明,龚治国,等.外包钢套法加固震损钢筋混凝土框架抗震性能试验研究[J].建筑结构,2013,43(12):67-73.Yin Jie,Zhu Chunming,Gong Zhiguo et al.Experimental study on seismic performance of earthquakedamaged RC frame strengthened by enveloped steel[J].Building Structure,2013,43(12):67-73.(in Chinese)
    [4]翁大根,张超,夏敬德,等.震损框架节点外包钢板加固试验研究[J].土木工程学报,2013,46(4):36-45.Weng Dagen,Zhang Chao,Xia Jingde,et al.Experimental study on earthquake-damaged frame joints strengthened with steel-enveloped plates[J].China Civil Engineering Journal,2013,46(4):36-45.(in Chinese)
    [5]余江滔,陆洲导,张克纯.震损钢筋混凝土框架节点修复后抗震性能试验研究[J].建筑结构学报,2010.12,31(12):64-73.Yu Jiangtao,Lu Zhoudao,Zhang Kechun.Experimental study on seismic behavior of strengthened RC column-beam joints damaged by simulated earthquake[J].Journal of Building Structure,2010.12,31(12):64-73.(in Chinese)
    [6]唐波,余江滔,丁斌.钢筋混凝土框架节点震损加固方法的对比研究[J].土木建筑与环境工程,2010.12,第32卷增刊2:339-341.Tang Bo,Yu Jiangtao,Ding Bin.Comparative study on the strengthening approach of RC column-beam joints damaged by simulated earthquake[J].Journal of Civil,Architectural and Environmental Engineering,2010.12,32(S2):339-341.(in Chinese)
    [7]王焕杰.外包钢套法加固混凝土框架节点抗震性能试验研究[D].上海:同济大学,2008.Wang Huanjie.Experimental study on the seismic performance of enveloped steel strengthened RC frame joint[D].Shanghai:Tongji University,2008.(in Chinese)
    [8]Karayannis C G,Sirkelis G M.Strengthening and rehabilitation of RC beam-column joints using carbonFRP jacketing and epoxy resin injection[J].Earthquake and Structural Dynamics,2008,37(5):769-790.
    [9]张宇,崔熙光,杨栋,等.重度损伤钢筋混凝土柱修复后的抗震性能研究[J].工业建筑,2011,41(7):38-44.Zhang Yu,Cui Xiguang,Yang Dong,et al.Experimental investigation on the seismic behaviors of repaired seriously damaged reinforced concrete columns[J].Industrial Construction,2011,41(7):38-44.(in Chinese)
    [10]林玮,孙伟,李宗津.连续碳纤维织布-氯氧镁水泥浆加固贴层的直剪研究[J].建筑材料学报,2011,14(1):106-110.Lin Wei,Sun Wei,Li Zongjin.Direct shear study of strengthening layer made of continuous carbon fiber fabric-magnesium oxychloride cement paste[J].Journal of Building Material,2011,14(1):106-110.(in Chinese)
    [11]陈忠范,万黎黎,李建龙,等.无机胶粘贴纤维布加固钢筋混凝土梁高温性能试验研究[J].四川建筑科学研究,2007,33(增刊):169-173.Chen Zhongfan,Wan Lili,Li Jianlong,et al.Experimental study on behaviors of RC beams strengthened with inorganic adhesive sticked FRP sheets at elevated temperature[J].Sichuan Building Science,2007,33(S):169-173.(in Chinese)
    [12]韩菊红.新老混凝土粘结断裂性能研究及工程应用[D].大连理工大学博士学位论文,2002.Han Juhong.Study on fracture performance and engineering application of adherence of new and old concrete[D].Dalian:Dalian University of Technology,2002.(in Chinese)
    [13]程红强.纤维混凝土与老混凝土粘结性能试验研究[D].郑州:郑州大学,2007.Cheng Hongqiang.Experimental research on adherence property of fresh fiber reinforced concrete to old concrete[D].Zhengzhou:Zhengzhou University,2007.(in Chinese)
    [14]王楠,徐世烺.超高韧性水泥基复合材料与既有混凝土粘结性能[J].建筑材料学报,2011,14(3):317-323.Wang Nan,Xu Shilang.Bonding performance between ultra high toughness cemetitous composites and existing concrete[J].Journal of Building Material,2011,14(3):317-323.(in Chinese)
    [15]李哲,杨水成,张浩博,等.岩石与混凝土界面裂缝的断裂能及断裂韧度[J].西北水资源与水工程,1998,9(1):42-45.Li Zhe,Yang Shuicheng,et al.Fracture energy and fracture toughness of the interfacial crack between rock and concrete[J].Water Resources and Water Engineering,1998,9(1):42-45.(in Chinese)
    [16]Coronado C A,Lopez M M.Experimental characterization of concrete-epoxy interfaces[J].Journal of Materials in Civil Engineering,2008,20(4):303-312.
    [17]Lau D,Büyükztürk O.Fracture characterization of concrete/epoxy interface affected by moisture[J].Mechanics of Materials,2010,42(12):1031-1042.
    [18]徐世烺.混凝土断裂力学[M].北京:科学出版社出版,2011:237-259.XU Shilang.Fracture Mechanics of Concrete[M].BEIJING:Science Press,2011:237-259.(in Chinese)
    [19]徐世烺,赵国藩.混凝土结构裂缝扩展的双K断裂准则[J].土木工程学报,1992,25(2):32-38.Xu Shilang,Zhao Guofan.A double-K Fracture criterion for the crack propagation in concrete structures[J].China Civil Engineering Journal,1992,25(2):32-38.(in Chinese)
    [20]赵艳华,徐世烺,吴智敏.混凝土结构裂缝扩展的双G准则[J].土木工程学报,2004,37(10):13-18.Zhao Yanhua,Xu Shilang,Wu Zhimin.A dual-G criterion for crack propagation in concrete structures[J].China Civil Engineering Journal,2004,37(10):13-18.(in Chinese)

版权所有:© 2021 中国地质图书馆 中国地质调查局地学文献中心