混凝土拉伸荷载条件下细观破损过程的CT试验研究
详细信息 本馆镜像全文    |  推荐本文 | | 获取馆网全文
摘要
对静力、动力拉伸荷载条件下混凝土的细观破损过程进行了CT试验研究,获得了试样内部裂纹萌生、扩展、贯通的全过程CT图像。通过对CT图像及图像兴趣区中整体统计区域、局部统计区域CT数均值的分析,研究了混凝土拉伸荷载条件下细观破损过程。结果表明:静力拉伸荷载条件下,裂纹在界面的薄弱区域形成后逐渐往相邻的薄弱部位扩展,两个统计区域CT数均值呈降低趋势,试样破坏时伴有少量骨料被拉断的现象;动力拉伸荷载条件下,裂纹从界面薄弱区域形成后追随最快的路径扩展,局部统计区域CT数均值呈下降趋势,而整体统计区域CT数均值变化幅度较小,破坏后骨料沿界面脱离砂浆粘结,且试样破裂面更为平整;由于加载速率的提高,骨料被拉断的现象非常显著。
The real time scanning observation on meso damage process in concrete was carried out using CT technology.CT images of crack propagation,coalescence and failure were obtained under static and dynamic tension.Meso-damage mechanism of concrete under tension was analyzed the mean CT numbers in large statistical region small statistic region of scanning layers ROI.The results showed that the cracks developed in the interface of weak region and expanded to adjacent weak partsthe mean CT numbers of the two statistical regions showed decreasing trend.Parts of aggregates were ruptured when the concrete wasdamaged under static tension.While in small statistic region,the cracks developed in the interface of weak region and expanded along the fastest path,and the mean CT numbers showed a decreasing trend The mean CT numbers in large statistical region changed slightly.The aggregate divorced from mortar along interface,and the failure plane was smoother when the concrete was damaged under dynamic tension.So,the aggregate was ruptured obviously because the loading rate was higher.
引文
[1]陈厚群,丁卫华,蒲毅彬,等.单轴压缩条件下混凝土细观破裂过程的X射线CT实时观测[J].水利学报,2006,37(9):1044-1050.Chen H Q,Ding W H,Pu Y B,et al.Real time observation on meso fracture process of concrete using X-ray CT under uniaxial compressive condition[J].Journal of Hydraulic Engineering,2006,37(9):1044-1050.(in Chinese)
    [2]丁卫华,陈厚群,张建军,等.高应变率作用下混凝土破裂过程的X射线CT观测[J].建筑结构学报,2006(Sup2):758-762.Ding W H,Chen H Q,Zhang J J,et al.X-ray CT detecting on concrete fracture process under high strain rate[J].Journal of Building Structures,2006(Sup2):758-762.(in Chinese)
    [3]党发宁,刘彦文,丁卫华,等.基于破损演化理论的混凝土CT图像定量分析[J].岩石力学与工程学报,2007,26(8):1588-1594.Dang F N,Liu Y W,Ding W H,et al.Quantitative analysis of concrete CT image based on damage-fracture evolution theory[J].Chinese Journal of Rock Mechanics and Engineering,2007,26(8):1588-1594.(in Chinese)
    [4]田威,党发宁,陈厚群.基于图像处理技术的混凝土细观动力破损过程CT分析[J].水利发电学报,2009,28(5):147-151.(in Chinese)Tian W,Dang F N,Chen H Q.CT analysis on dynamic meso-fracture process of concrete based on the image processing[J].Journal of Hydroelectric Engineering,2009,28(5):147-151.(in Chinese)
    [5]Wong R C K,Chau K T.Estimation of air void and aggregate spatial distributions in concrete under uniaxial compression using computer tomography scanning[J].Cement and Concrete Research,2004,35:1566-1576.
    [6]Man H K,van Mier J G M.Damage distribution and size effect in numerical concrete from lattice analyses[J].Cement and Concrete Composites,2011,33(9):867-880.
    [7]Jivkov A P,Engelberg D L,Stein R.Pore space and brittle damage evolution in concrete[J].Engineering Fracture Mchanics,2013,110:378-395.
    [8]Piotrowska E,Malecot Y,Ke Y.Experimental investigation of the effect of coarse aggregate shape and composition on concrete triaxial behavior[J].Mechanics of Materials,2014,79:45-57.
    [9]田威,党发宁,梁昕宇,等.混凝土细观损伤特性的CT研究[J].实验力学,2009,24(3):184-190.Tian W,Dang F N,Liang X Y,et al.CT real-time observation of the meso-damage process for concrete material under uniaxial compression[J].Journal of Experiment Mechanics,2009,24(3):184-190.(in Chinese)
    [10]田威,党发宁,陈厚群.动力荷载作用下混凝土破裂特征CT试验研究[J].地震工程与工程振动,2011,24(1):30-34.Tian W,Dang F N,Chen H Q.CT experimental study of failure characteristics of concrete under dynamic loading[J].Journal of Earthquake Engineering and Engineering Vibration,2011,24(1):30-34.(in Chinese)
    [11]田威,党发宁,陈厚群.适于CT试验的动态加载设备研制及其应用[J].岩土力学,2010,31(1):329-313.Tian W,Dang F N,Chen H Q.Development and application of the dynamic loading apparatus on CT experiment[J].Rock and Soil Mechanics,2010,31(1):329-313.(in Chinese)
    [12]田威,党发宁,陈厚群.基于单轴压缩CT试验的混凝土细观破损分区研究[J].水利学报,2011,42(8):124-130.Tian W,Dang F N,Chen H Q.Research on meso damage-fracture divisional zones of concrete based on uniaxial compression CT experiment[J].Journal of Hydraulic Engineering,2011,42(8):124-1 30(in Chinese)
    [13]张健.大岗山拱坝混凝土动力特性CT试验研究[D].西安:西安理工大学,2010:3.

版权所有:© 2023 中国地质图书馆 中国地质调查局地学文献中心