废弃牛毛水解液制备蛋白基液体地膜的研究

详细信息    查看全文 | 推荐本文 |

英文篇名：Study on preparation of protein-based liquid agricultural film with hydrolyzate from cowhair waste 作者：李闻欣 ; 陈玉柔 ; 张素风 英文作者：LI Wen-xin;CHEN Yu-rou;ZHANG Su-feng;College of Bioresources Chemical and Materials Engineering, Shaanxi University of Science & Technology; 关键词：牛毛角蛋白 ; 水解 ; 聚乙烯醇 ; 液体地膜 英文关键词：bovine hair keratin;;hydrolysis;;polyvinyl alcohol;;liquid agricultural film 中文刊名：陕西科技大学学报 英文刊名：Journal of Shaanxi University of Science & Technology 机构：陕西科技大学轻工科学与工程学院; 出版日期：2019-05-29 出版单位：陕西科技大学学报 年：2019 期：03 基金：陕西省教育厅重点实验室科研计划项目(17JS016);; 生物质化学与材料国际联合研究中心项目(2018GHJD-19) 语种：中文; 页：12-18 页数：7 CN：61-1080/TS ISSN：2096-398X 分类号：X705

摘要

废弃固体蛋白资源化利用和农用地膜的"白色污染"均是目前急需解决的热点问题.研究采用碱氧化法水解废弃牛毛,将牛毛水解蛋白液与PVA、戊二醛和甘油共混制作液体地膜并表征其理化性能.以共混膜的不挥发物含量、拉伸强度、断裂伸长率以及在水中的溶胀性等为指标,单因素法考查了水解液与PVA的质量比、戊二醛用量、甘油用量、共混温度和时间等因素对共混膜性能的影响.研究优化的制膜工艺为:水解液与PVA质量比8∶1,甘油0.3 g,戊二醛0.2 g,温度100℃,时间40 min.采用XRD、FT-IR和DSC等手段对共混膜的结构和性能进行表征.共混膜热稳定性较好、具有保温保湿和促进农作物生长等性能.
        The "white pollution"of agricultural film and rejected solid protein resource utilizationis a hot issue that needs to be solved urgently.The alkali oxidization method was used to hydrolyze the waste cow hair,and the hydrolyzed protein solution of bovine hair was blended with PVA,glutaraldehyde and glycerin to prepare a liquid film and its physical and chemical properties were characterized.The non-volatile content,tensile strength,elongation at break and swellability in water were used as indicators to analyze the single factor method.The effects of the mass ratio of hydrolysate to PVA,the amount of glutaraldehyde,the amount of glycerin,the blending temperature and the blending time on the properties of the blended membrane were investigated.The structure and properties of the blend membrane were characterized by XRD,FT-IR and DSC.The experimental results show that the optimal membrane preparation process:Hydrolysate and PVA mass 8∶1,glycerol 0.3 g,glutaraldehyde 0.2 g,temperature is 100 ℃,time 40 min.The blend membrane not only has the properties of good thermal stability,heat preservation and moisturization,and promotes the growth of crops,but also reduces environmental pollution and realizes the resource utilization of tannery waste.

引文

[1] 宋超.聚乙烯地膜残留对作物产量/土壤质量以及土壤微生物群落组成的影响[D].兰州:兰州大学,2014.
    [2] Immirzi B,Santagataa G,Vox G,et al.Preparation,characterization and field-testing of a biodegradable sodium alginspray mulch[J].Biosystems Engineering,2009,102(4):461-472.
    [3] Tan Z,Yi Y,Wang H,et al.Physical and degradable properties of mulching films prepared from natural fibers and biodegradable polymers[J].Applied Sciences,2016,6(5):147.
    [4] 毛培.保毛脱毛回收牛毛降解制备皮革填充材料的研究[D].温州:温州大学,2014.
    [5] 崔国廉,王晓龙,但年华,等.牛毛水解方法的优化及产物性能表征[J].皮革科学与工程,2013,23(6):19-25.
    [6] 谭小军,曹贝荣,王全杰.制革废弃牛毛碱水解条件的优化[J].西部皮革,2010,32(13):8-11.
    [7] Villa A L V,Arago M R S,Dos Santos E P,et al.Feather keratin hydrolysates obtained from microbial keratinases:Effect on hair fiber[J].BMC Biotechnology,2013,13:15-16.
    [8] 刘萌,程海明.牛毛的水解及水解产物性能的分析[J].中国皮革,2012,41(17):27-31.
    [9] 昝大鑫,陈莹,许莉.羊毛角蛋白膜的制备及其气体分离性能的研究[J].膜科学与技术,2005,25(5):45-49.
    [10] 袁祖纯,黄水旺,吴红熹,等.羊毛角蛋白膜的制备和热性能分析[J].纺织科技进展,2012(2):36-38.
    [11] 陈宗良.角蛋白基可生物降解地膜的研制[D].西安:陕西科技大学,2009.
    [12] 郝亮.液体地膜研制及其保水效应[D].北京:中国科学院大学,2013.