为研究老化对泡沫温拌沥青混合料性能的影响,采用体积指标法确定泡沫温拌Sup-20混合料的适宜成型温度,分别对不同老化时间下的泡沫温拌沥青混合料的体积指标以及原样混合料、短期老化后和长期老化后的热拌沥青混合料和泡沫温拌沥青混合料的高温性能、低温性能和水稳定性能进行研究。结果表明:泡沫温拌Sup-20混合料适宜的压实温度为110℃左右,拌和温度为125℃左右。泡沫温拌Sup-20混合料的高温抗车辙性能、低温抗裂性能和水稳定性能均稍弱于相应的热拌沥青混合料,并且泡沫温拌Sup-20混合料的路用性能衰减程度大于热拌混合料,其抗老化性能弱于热拌混合料。
In order to study the effect of aging on properties of foamed warm-mixed asphalt mixture,volume index method was used to determine the optimum forming temperature of the foamed asphalt mixture.Road performance of original hot-mixed asphalt mixture and the foamed warm-mixed asphalt mixture under different conditions(original,short term aging,long term aging)was investigated through laboratory tests.Test results show that the optimal compaction temperature of Sup-20 foamed asphalt mixture is about 110℃,and the mixing temperature is about 125℃.High temperature performance,low temperature crack resistance and water stability of Sup-20 foamed asphalt mixture are weaker than that of hot-mixed asphalt mixture,the attenuation of road performance of Sup-20 foamed asphalt mixture is higher than that of hot-mixed asphalt mixture,and its aging resistance is lower than that of hot-mixed asphalt mixture.
引文
[1]杨彦海,高小晰,沈阳,等.温拌沥青技术在低温施工中的应用[J].中外公路,2014,34(3):264~267.
[2] Yu X, Wang Y, Luo Y.Impacts of Water Content on Rheological Properties and Performance-related Behaviors of Foamed Warm-mix Asphalt[J].Construction and Building Materials,2013,48(11):203~209.
[3]石津金.泡沫沥青温拌技术应用研究[D].天津:河北工业大学,2014.
[4]徐晓和,李寿伟,邹晓勇.SBS泡沫温拌沥青混合料路用性能研究[J].黑龙江交通科技,2015(1):7~9.
[5]徐波,王凯,周王成.基于改进车辙因子的泡沫沥青高温性能评价[J].材料科学与工程学报,2015,33(6):899~902.
[6] Kemp G R,Predoehl N H.A Comparison of Field and Laboratory Environments on Asphalt Durability[C]//Association of Asphalt Paving Technologists Proceedings,1981,50:492~537.
[7] Xu S,Yu J,Zhang C,et al.Effect of Ultraviolet Aging on Rheological Properties of Organic Intercalated Layered Double Hydroxides Modified Asphalt[J].Construction and Building Materials,2015,75:421~428.
[8]张保立.沥青与沥青混合料光热老化路用性能研究[D].重庆交通大学,2010.
[9]刘彦,朱国军,王小磊,等.SMA-13与AC-13路面老化低温力学性能对比研究[J].公路,2010(10):193~198.
[10]陈华鑫,姜艺,李硕,等.沥青混合料老化后的低温性能[J].长安大学学报:自然科学版,2010(1):1~5.
[11]郭天惠,郭鹏.温拌再生沥青混合料压实温度的确定[J].中外公路,2012,32(3):42~45.
[12]黄康旭,梁星敏,徐波.RAP掺量对泡沫温拌再生沥青混合料路用性能的影响[J].材料科学与工程学报,2016,34(5):794~797.