Al-Si-Fe合金第二相形态控制技术研究
|
摘要
本文系统研究了不同种类的合金元素、变质、电磁搅拌及二次加热处理对Al-Si-Fe合金第二相形态影响规律。研究结果表明：红磷可以明显细化合金中的初晶硅，当加入量为0.3wt%时，取得最佳变质效果；锰、镍合金中加入后，通过形成多种复杂金属间化合物，细化针片状富铁相，减小铁对铝硅合金性能的危害；铜使合金微观组织发生粗化；电磁搅拌明显细化合金组织，使第二相圆整化，搅拌电压为200V时，取得最佳细化效果；二次加热使合金组织中产生部分液相，在650?C保温10min，取得适宜的液相量。
In this article the influence of modification, alloying elements, electro magnetic stirring and reheat on the Al-Si-Fe alloy is studied systematically. The result shows that modification can make the β-Si phase thin when the joining amount is 0.3wt%, making the best modification result. Alloying elements Mn and Ni are always used to neutralize iron's harm in aluminum alloys. They can form many kinds of complicated metallically compounds with Fe and Al, and eliminate needle-like iron-rich phases to reduce iron's harm in Al-Fe alloy. Copper makes the alloy microstructure thick and electromagnetic stirring obviously makes the alloy microstructure thin, round the second phase, when the stirring voltage is 200V, making the best result; Reheat makes liquid phases emerge in the alloy, when the warming temperature is 650?C and the warming time is 10 min, making the suitable liquid phase amount.
In this article the influence of modification, alloying elements, electro magnetic stirring and reheat on the Al-Si-Fe alloy is studied systematically. The result shows that modification can make the β-Si phase thin when the joining amount is 0.3wt%, making the best modification result. Alloying elements Mn and Ni are always used to neutralize iron's harm in aluminum alloys. They can form many kinds of complicated metallically compounds with Fe and Al, and eliminate needle-like iron-rich phases to reduce iron's harm in Al-Fe alloy. Copper makes the alloy microstructure thick and electromagnetic stirring obviously makes the alloy microstructure thin, round the second phase, when the stirring voltage is 200V, making the best result; Reheat makes liquid phases emerge in the alloy, when the warming temperature is 650?C and the warming time is 10 min, making the suitable liquid phase amount.
引文
1. 张蓉. 熔体过热处理对Al-Si过共晶合金凝固组织及耐磨性的影响. 西北工业大学博士论文: 西安. 2000
2. 袁晓光, 李英民. 制备工艺对铝硅铁挤压合金凝固组织的影响. 第二届中国国际压 铸会议论文集. 沈阳: 东北大学出版社, 2000
3. 羊秋林, 李尹熙. 汽车用轻量化材料. 北京: 机械工业出版社, 1991
4. 彭晓东, 李玉兰, 刘江. 轻合金在汽车上的应用. 机械工程材料, 1999, 23(2): 1~4
5. 雷广孝. 国内外铸造铝活塞材料的应用及研究概况. 特种铸造及有色合金, 1988(3): 44~49
6. 沈保罗, 吕旭东, 唐俊, 共晶和过共晶铝硅合金活塞尺寸稳定性的研究. 特种铸造及有色合金, 1996, 3: 42~43
7. 蔡宗德, 张连芳,孙建荣. 过共晶铝硅合金的生产及应用, 特种铸造及有色合金, 1990, 4: 37~39
8. 赵永治, 高泽生. 过共晶Al-Si合金连续铸造中初晶硅细化的新方法. 轻合金加工技术, 1995, 23(10): 5~8
9. 赵恒先, 陈润辉. 过共晶铝硅合金细化变质的进展. 轻金属, 1992, 2: 61~64
10. 毛卫民, 李树索, 赵爱民等. 电磁搅拌Al-24%Si合金的显微组织. 中国有色金属学报, 2001, 11(5): 819~823
11. 毛卫民, 李树索, 赵爱民等. 电磁搅拌过共晶Al-Si合金初生Si分布的影响. 金属学报, 2000, 10: 1~6
12. 刘昌明, 何乃军. 过共晶铝硅合金半固态挤压铸造近终成形技术研究. 金属成形工艺, 2000, 18(1): 38~4
13. Wolfgang Schneider. A new method for the Refinement of Primary Si of Hyper-
eutectic Al-Si Alloys in Direct chill and Ingot Casting. Light Metals, 1993: 815~820
14. 赖华清, 范宏训, 徐祥. 过共晶铝硅合金的研究及应用. 汽车工艺与材料, 2001, 10: 21~24
15. 邹裕厚. 过共晶铝硅合金的研制与生产. 特种铸造及有色合金, 1990, 5: 23~27
16. 龚建森等. 高效无公害铝硅合金用SR-813复合变质剂的研究. 特种铸造及有色合金, 1983, 3: 34~36
17. 孙德宝, 李克, 王俊等. 镧、钇稀土在过共晶铝硅合金中的作用. 上海交通大学学报, 1999, 33(7): 795~798
18. 袁晓光. 快速凝固高硅铝合金的微观组织及力学性能. 哈尔滨工业大学博士学位论文: 哈尔滨. 1997
19. C. F. Dxion, H. M. Skelly. Al-Si Alloys Prepared by Spinning Melt. Int. J. Powder Metall.. 1965, 1(4): 28~33
20. H. M. Skelly, C. F. Dixon. Al-Si Power Metallurgy Alloys. Int. J. Power Metall.. 1971, 7(3): 47~52
21. J. Zhou, J. Duszozyk. Mechanical Response and Structural Development during the Hot Extrusion of a Rapidly Solidified Al Alloy Power. J. Mater. Sci.. 1992, 27, 27: 3856~3863
22. 王峰, 杨滨, 崔华等. 喷射沉积Al-Si-Ni-Cu-Mg合金的显微组织和相组成. 特种铸造及有色合金, 2000, 4: 1~3
23. 李元元, 张大童, 夏伟等. 高压水雾化法制备高硅铝合金粉末特性. 金属学报, 1998, 34(1): 95~99
24. 袁晓光, 黄景福, 张哲等. 双级雾化水冷Al-Si-Fe合金微观组织及性能. 材料研究学报, 2001, 15(2): 186~191
25. Y. Odani. Powder Forged Al Alloy to Challenge Ferrous Metals. Metal Powder Report. 1994, 49: 36~41
26. 孙赞业, 于敞, 厉松春等. 铁在铝硅合金中存在的形态及其作用分析. 铸造, 1998, 7: 42~46
27. 祝汉良等, A357合金中铁的有害作用. 铸造, 1996(5): 9～12
28. J. E. Hatch. Aluminum: Properties and Physical Metallurgy. ASM International, Metal Park, OH(1984)
29. P. N. Crepeau. Effect of Iron in Al-Si Casting Alloys. AFS Transactions, 1995, 103: 361~365
30. W. Bonsack. Iron the Problematic Factor in Quality of Aluminum Alloy Die Castings. AFS Transactions, 1961, 69: 712~720
31. 黄健, 李洪涛, 王汝耀. Fe对Al-Si活塞合金强度的影响. 兵器材料科学与工程, 1990, 4: 1~7
32. F. A. Badia. Effect of Composition and heat Treatment on the Tensile Properties of an Al11.5Si5Ni Casting Alloy. Modern Castings, 1996, 50: 104~115
33. 谭锁奎, 任全宝. 金属型铸造活塞铝合金中铁的作用研究. 特种铸造及有色合金, 1998, 3: 31～33
34. 林小征, 印飞, 孙宝德. 铁对铝硅合金性能的影响及抵消其有害作用的措施. 铸造技术, 1999, 5: 29~32
35. 王祝堂, 张振录. 铝合金的组织与性能. 北京: 冶金工业出版社,1988
36. Bian X. F, Chen J. H. Intensifying the effect of Mg or Sb Modification of Al-Si Alloy. JOM, 1997(2), 35~36
37. Mondolfo L. F. Aluminum Alloys: Structure and Properties. Butterworth, Alondon- Boston, 1976
38. N.A.Belov, A.A.Aksenov and D.G.Eskin. Iron in Aluminum Alloys. London: Taloy & Francis Inc, 2002
39. 程钢. 复合处理制备半固态过共晶铝硅合金的研究. 昆明理工大学硕士学位论文: 昆明, 2001
40. 印飞, 王亦新, 洪慎章等. 半固态铸造铝合金材料的研究现状. 特种铸造及有色合金, 2000, 3: 44~46
41. 张伟强. 共晶合金在电磁力离心复合作用下的凝固规律. 中国科学院金属研究所博士学位论文: 沈阳, 1997
42. J. P. Birat and J. Chone. Ironmaking and Steelmaking, 1983, 10(6): 269~275
43. Flemings M C. Behavior of metal alloys in the semi-solid state. Metallurgical Transactions B, 1991, 22B(7): 269~293
44. 张勤, 路贵民,崔建忠等. CREM法半连续铸造Al合金非枝晶组织的形成机制. 金属学报, 2001, 37(8): 873~876
45. Hellawell A. Grain evolution in conventional and rheo-castings. Proceedings of the 4th International Conference on Semi-solid Processing of Alloys and Composites. Sheffi- eld, 1996: 60~65
46. 张奎, 刘国钧, 张永忠等. 半固态金属制备原理与应用 稀有金属. 1998, 22(6): 447~449
47. 李树索, 赵爱民, 毛卫民等. 半固态过共晶Al-Si合金显微组织中近球形α相形成机理的研究. 金属学报, 2000, 36(5): 545~549
48. 吴炳尧, 戴挺. 半固态触变成形坯料二次加热技术分析. 特种铸造及有色合金, 2000, 6: 58~61
49. 张大辉, 毛卫民, 钟雪友等. 重熔温度对半固态AlSi7Mg合金变形性的影响. 热加工工艺, 2000, 5: 15~17
50. J. Zhou, J. Duszczyk, B. M. Korevaar. Structural Characteristics of a Nickel-Modified Al-20Si-3Cu-1Mg Alloy Powder. Mater. Sci., 1992, 27: 3341~3356
51. 陆文华, 李隆盛, 黄良余. 铸造合金及其熔炼. 北京: 机械工业出版社, 1997
52. 印飞, 杨江波, 王亦新等. 铝硅合金中针状铁相的断裂现象. 特种铸造及有色合金, 2000, 2: 1~2
53. 胡建刚. 耐磨AlSiFe合金第二相形态及控制. 沈阳工业大学硕士学位论文: 沈阳. 2003
54. 陆松, 许广济, 陈体军. 等温处理对半固态ZA27组织演变的影响. 热加工工艺, 2000, 1: 42~47
2. 袁晓光, 李英民. 制备工艺对铝硅铁挤压合金凝固组织的影响. 第二届中国国际压 铸会议论文集. 沈阳: 东北大学出版社, 2000
3. 羊秋林, 李尹熙. 汽车用轻量化材料. 北京: 机械工业出版社, 1991
4. 彭晓东, 李玉兰, 刘江. 轻合金在汽车上的应用. 机械工程材料, 1999, 23(2): 1~4
5. 雷广孝. 国内外铸造铝活塞材料的应用及研究概况. 特种铸造及有色合金, 1988(3): 44~49
6. 沈保罗, 吕旭东, 唐俊, 共晶和过共晶铝硅合金活塞尺寸稳定性的研究. 特种铸造及有色合金, 1996, 3: 42~43
7. 蔡宗德, 张连芳,孙建荣. 过共晶铝硅合金的生产及应用, 特种铸造及有色合金, 1990, 4: 37~39
8. 赵永治, 高泽生. 过共晶Al-Si合金连续铸造中初晶硅细化的新方法. 轻合金加工技术, 1995, 23(10): 5~8
9. 赵恒先, 陈润辉. 过共晶铝硅合金细化变质的进展. 轻金属, 1992, 2: 61~64
10. 毛卫民, 李树索, 赵爱民等. 电磁搅拌Al-24%Si合金的显微组织. 中国有色金属学报, 2001, 11(5): 819~823
11. 毛卫民, 李树索, 赵爱民等. 电磁搅拌过共晶Al-Si合金初生Si分布的影响. 金属学报, 2000, 10: 1~6
12. 刘昌明, 何乃军. 过共晶铝硅合金半固态挤压铸造近终成形技术研究. 金属成形工艺, 2000, 18(1): 38~4
13. Wolfgang Schneider. A new method for the Refinement of Primary Si of Hyper-
eutectic Al-Si Alloys in Direct chill and Ingot Casting. Light Metals, 1993: 815~820
14. 赖华清, 范宏训, 徐祥. 过共晶铝硅合金的研究及应用. 汽车工艺与材料, 2001, 10: 21~24
15. 邹裕厚. 过共晶铝硅合金的研制与生产. 特种铸造及有色合金, 1990, 5: 23~27
16. 龚建森等. 高效无公害铝硅合金用SR-813复合变质剂的研究. 特种铸造及有色合金, 1983, 3: 34~36
17. 孙德宝, 李克, 王俊等. 镧、钇稀土在过共晶铝硅合金中的作用. 上海交通大学学报, 1999, 33(7): 795~798
18. 袁晓光. 快速凝固高硅铝合金的微观组织及力学性能. 哈尔滨工业大学博士学位论文: 哈尔滨. 1997
19. C. F. Dxion, H. M. Skelly. Al-Si Alloys Prepared by Spinning Melt. Int. J. Powder Metall.. 1965, 1(4): 28~33
20. H. M. Skelly, C. F. Dixon. Al-Si Power Metallurgy Alloys. Int. J. Power Metall.. 1971, 7(3): 47~52
21. J. Zhou, J. Duszozyk. Mechanical Response and Structural Development during the Hot Extrusion of a Rapidly Solidified Al Alloy Power. J. Mater. Sci.. 1992, 27, 27: 3856~3863
22. 王峰, 杨滨, 崔华等. 喷射沉积Al-Si-Ni-Cu-Mg合金的显微组织和相组成. 特种铸造及有色合金, 2000, 4: 1~3
23. 李元元, 张大童, 夏伟等. 高压水雾化法制备高硅铝合金粉末特性. 金属学报, 1998, 34(1): 95~99
24. 袁晓光, 黄景福, 张哲等. 双级雾化水冷Al-Si-Fe合金微观组织及性能. 材料研究学报, 2001, 15(2): 186~191
25. Y. Odani. Powder Forged Al Alloy to Challenge Ferrous Metals. Metal Powder Report. 1994, 49: 36~41
26. 孙赞业, 于敞, 厉松春等. 铁在铝硅合金中存在的形态及其作用分析. 铸造, 1998, 7: 42~46
27. 祝汉良等, A357合金中铁的有害作用. 铸造, 1996(5): 9～12
28. J. E. Hatch. Aluminum: Properties and Physical Metallurgy. ASM International, Metal Park, OH(1984)
29. P. N. Crepeau. Effect of Iron in Al-Si Casting Alloys. AFS Transactions, 1995, 103: 361~365
30. W. Bonsack. Iron the Problematic Factor in Quality of Aluminum Alloy Die Castings. AFS Transactions, 1961, 69: 712~720
31. 黄健, 李洪涛, 王汝耀. Fe对Al-Si活塞合金强度的影响. 兵器材料科学与工程, 1990, 4: 1~7
32. F. A. Badia. Effect of Composition and heat Treatment on the Tensile Properties of an Al11.5Si5Ni Casting Alloy. Modern Castings, 1996, 50: 104~115
33. 谭锁奎, 任全宝. 金属型铸造活塞铝合金中铁的作用研究. 特种铸造及有色合金, 1998, 3: 31～33
34. 林小征, 印飞, 孙宝德. 铁对铝硅合金性能的影响及抵消其有害作用的措施. 铸造技术, 1999, 5: 29~32
35. 王祝堂, 张振录. 铝合金的组织与性能. 北京: 冶金工业出版社,1988
36. Bian X. F, Chen J. H. Intensifying the effect of Mg or Sb Modification of Al-Si Alloy. JOM, 1997(2), 35~36
37. Mondolfo L. F. Aluminum Alloys: Structure and Properties. Butterworth, Alondon- Boston, 1976
38. N.A.Belov, A.A.Aksenov and D.G.Eskin. Iron in Aluminum Alloys. London: Taloy & Francis Inc, 2002
39. 程钢. 复合处理制备半固态过共晶铝硅合金的研究. 昆明理工大学硕士学位论文: 昆明, 2001
40. 印飞, 王亦新, 洪慎章等. 半固态铸造铝合金材料的研究现状. 特种铸造及有色合金, 2000, 3: 44~46
41. 张伟强. 共晶合金在电磁力离心复合作用下的凝固规律. 中国科学院金属研究所博士学位论文: 沈阳, 1997
42. J. P. Birat and J. Chone. Ironmaking and Steelmaking, 1983, 10(6): 269~275
43. Flemings M C. Behavior of metal alloys in the semi-solid state. Metallurgical Transactions B, 1991, 22B(7): 269~293
44. 张勤, 路贵民,崔建忠等. CREM法半连续铸造Al合金非枝晶组织的形成机制. 金属学报, 2001, 37(8): 873~876
45. Hellawell A. Grain evolution in conventional and rheo-castings. Proceedings of the 4th International Conference on Semi-solid Processing of Alloys and Composites. Sheffi- eld, 1996: 60~65
46. 张奎, 刘国钧, 张永忠等. 半固态金属制备原理与应用 稀有金属. 1998, 22(6): 447~449
47. 李树索, 赵爱民, 毛卫民等. 半固态过共晶Al-Si合金显微组织中近球形α相形成机理的研究. 金属学报, 2000, 36(5): 545~549
48. 吴炳尧, 戴挺. 半固态触变成形坯料二次加热技术分析. 特种铸造及有色合金, 2000, 6: 58~61
49. 张大辉, 毛卫民, 钟雪友等. 重熔温度对半固态AlSi7Mg合金变形性的影响. 热加工工艺, 2000, 5: 15~17
50. J. Zhou, J. Duszczyk, B. M. Korevaar. Structural Characteristics of a Nickel-Modified Al-20Si-3Cu-1Mg Alloy Powder. Mater. Sci., 1992, 27: 3341~3356
51. 陆文华, 李隆盛, 黄良余. 铸造合金及其熔炼. 北京: 机械工业出版社, 1997
52. 印飞, 杨江波, 王亦新等. 铝硅合金中针状铁相的断裂现象. 特种铸造及有色合金, 2000, 2: 1~2
53. 胡建刚. 耐磨AlSiFe合金第二相形态及控制. 沈阳工业大学硕士学位论文: 沈阳. 2003
54. 陆松, 许广济, 陈体军. 等温处理对半固态ZA27组织演变的影响. 热加工工艺, 2000, 1: 42~47
© 2004-2018 中国地质图书馆版权所有 京ICP备05064691号 京公网安备11010802017129号 地址：北京市海淀区学院路29号 邮编：100083 电话：办公室：(+86 10)66554848；文献借阅、咨询服务、科技查新：66554700 |