H13钢激光填丝仿生耦合热疲劳性能分析

详细信息    查看全文 | 推荐本文 |

英文篇名：Investigation on thermal fatigue property of H13 steel with biomimetic units processed by laser welding with filler wire 作者：刘立君 ; 于义涛 ; 贾志欣 ; 陈光圆 英文作者：LIU Lijun;YU Yitao;JIA Zhixin;CHEN Guangyuan;School of Material Science and Engineering,Harbin University of Science and Technology;Ningbo Institute of Technology, Zhejiang University;Ningbo Donghao Die-casting Co.,Ltd.; 关键词：仿生强化 ; 热疲劳裂纹 ; H13钢 ; 激光熔凝 ; 激光填丝 英文关键词：biomimetic;;thermal fatigue crack;;H13 steel;;laser remelting;;laser welding with filler wire 中文刊名：HJXB 英文刊名：Transactions of the China Welding Institution 机构：哈尔滨理工大学材料科学与工程学院;浙江大学宁波理工学院;宁波东浩铸业有限公司; 出版日期：2019-03-25 出版单位：焊接学报 年：2019 期：v.40 基金：国家自然科学基金资助项目(51275468);; 浙江省自然基金资助项目(LY17E050013);; 哈尔滨市科技创新人才创新基金(2017RAXXJ012);; 宁波市工业重大项目(2017B10027) 语种：中文; 页：HJXB201903002 页数：6 CN：03 ISSN：23-1178/TG 分类号：12-16+167

摘要

热疲劳龟裂是铝合金压铸模具的主要失效模式.针对这一现象,利用激光表面熔凝技术及激光表面填丝技术耦合仿生强化模型对压铸模具表面进行强化,分析不同处理方式下热疲劳裂纹扩展形态,探索提高压铸模具寿命的方法.试验利用Nd:YAG激光器对试样进行加工,每隔500次热疲劳循环后,观察不同试样裂纹扩展情况,5 000次循环后得出裂纹扩展形貌.结果表明,经过激光表面填丝技术处理所得的仿生单元体硬度相对于激光表面熔凝处理所得单元体略有提高,经激光表面填丝技术处理的试样具有更高的抗热疲劳性能.
        Thermal fatigue crack is the main failure mode of aluminum alloy die-casting dies. According to the phenomenon, an attempt to harden the working surface of diecasting dies with biomimetic units was made by using biomimetic coupled laser welding with filler wire process and laser remelting process, respectively. The propagation of thermal fatigue crack was analysed under different treatments.The ways to improve die service life was explored. The samples of this experiment was processed by Nd:YAG laser.The thermal fatigue cracks were measured or observed at intervals of 500 cycles and the morphology of thermal fatigue cracks was obtained after 5 000 cycles. The experimental results show that the microhardness of biomimetic units that was made by laser welding with filler wire is slightly above the biomimetic units that was made by laser remelting process,samples that is processed by laser welding with filler wire have better thermal fatigue resistance ability.

引文

[1]Telasang G,Msjurmdar Dutta J,Padmanabham G,et al.Structureproperty correlation in laser surface treated ANSI H13 tool steel for improved mechanical properties[J].Mater Science and Engineering,2014,A 599:255-67.
    [2]刘立君,齐萌,于义涛,等.TIG填丝+激光熔凝模具修复工艺研究[J].焊接学报,2018,39(4):73-78.Liu Lijun,Qi Meng,Yu Yitao,et al.The property of die-casting dies repaired by manual TIG filler wire coupling laser melting[J].Transactions of the China Welding Institution,2018,39(4):73-78.
    [3]Zhang Z H,Zhou H,Ren L Q,et al.Effect of units in different sizes on thermal fatigue behavior of 3Cr2W8V die steel with biomimetic non-smooth surface[J].International Journal of Fatigue,2009,31:468-75.
    [4]Jia Z X,Li J Q,Liu L J,et al.Performance enhancements of highpressure die-casting die processed by biomimetic laser-remelting process[J].International Journal of Advanced Manufacturing Technology,2012,58:421-9.
    [5]刘红兵,陶汪,陈洁,等.激光填丝焊焊丝熔入行为特征[J].焊接学报,2013,34(11):73-77.Liu Hongbing,Wang Tao,Chen Jie,et al.The characteristics on the behavior of welding wire melting in the laser welding with filler wire[J].Transactions of the China Welding Institution,2013,34(11):73-77.
    [6]刘立君,于义涛,金海平,等.基于ROI区域特征模具激光修复熔池填丝熔入状态识别技术[J].焊接学报,2017,38(11):7-10.Liu Lijun,Yu Yitao,Jin Haiping,et al.Identification technology of the state of wire melting into the molten pool during laser repairing mold based on ROI area’s features[J].Transactions of the China Welding Institution,2017,38(11):7-10.
    [7]Tsay L W,Liu Y C,Lin D Y,et al.The use of laser surface-annealed treatment to retard fatigue crack growth of austenitic stainless steel[J].Mater Science and Engineering,2004,A384:177-183.