采用传统固相反应法制备CaTiO_3掺杂Mg2B2O5微波介电陶瓷。使用X线衍射仪(XRD)、扫描电子显微镜(SEM)和微波介电性能测试等手段,研究了CaTiO_3掺杂对样品微观结构和微波介电性能的影响。结果表明,Mg_2B_2O_5相和CaTiO_3相二者能够共存,随着CaTiO_3掺杂量的增加介电常数和谐振频率温度系数会增大,而品质因数会有所下降。当CaTiO_3的质量分数为5%时,样品在1 085℃烧结4h后获得了最佳微波介电性能,即介电常数εr=7.03,品质因数Q×f=42 221GHz,谐振频率温度系数τf=-2.8×10~(-6)℃-1。
The CaTiO_3 doping Mg_2B_2O_5 microwave dielectric ceramics were synthesized by the traditional solidstate reaction method.The effects of CaTiO_3 doping on the microwave dielectric properties and micro structure of the samples were studied using XRD,SEM and microwave dielectric properties measurements.The results show that the Mg_2B_2O_5 and CaTiO_3 phases can coexist,and the dielectric constant and the temperature coefficient of resonant increase with the increase of the content of CaTiO_3 while the quality factor slightly decreases.When the mass fraction of Mg_2B_2O_5 is 5%,the CaTiO_3 ceramics sample sintered at 1 085℃ for 4h shows optimal properties,that is,εr=7.03,Q×f=42 221 GHz,τf=-2.8×10~(-6)℃-1.
引文
[1]余韶阳,李恩竹,周晓华,等.Li2O-Nb2O5-TiO2微波介电陶瓷掺杂改性研究[J].压电与声光,2014,36(4):621-624.YU Shaoyang,LI Enzhu,ZHOU Xiaohua,et al.Study on doping modification of microwave dielectric Li2O-Nb2O5-TiO2ceramics[J].Piezoelectrics&Acoustoopics,2014,36(4):621-624.
[2]WU S,SONG K,LIU P,et al.Effect of TiO2doping on the structure and microwave dielectric properties of cordierite ceramics[J].Journal of the American Ceramic Society,2015,98(6):1842.
[3]YI L,LI L,LIU X Q,et al.Structure evolution and enhanced microwave dielectric characteristics of(Sr1-xCax)La2Al2O7ceramics[J].Journal of the American Ceramic Society,2014,97(11):3531.
[4]ZHANG J,YUE Z,ZHOU Y,et al.Microwave dielectric properties and thermally stimulated depolarization currents of(1-x)MgTiO3-xCa0.8Sr0.2TiO3ceramics[J].Journal of the American Ceramic Society,2015,98(5):1548-1554.
[5]DOSLER U,KRZMANC M M,JAN CAR B,et al.Ahigh-Q microwave dielectric material based on Mg3B2O6[J].Journal of the American Ceramic Society,2010,93(11):3788-3792.
[6]UYILDIZ A,GIRGIN.Controlled synthesis,characterization and thermal properties of Mg2B2O5[J].Open Chemistry,2010,8(4):758-765.
[7]DOSLER U,KRZMANC M M,SUVOROV D.The synthesis and microwave dielectric properties of Mg3B2O6and Mg2B2O5 ceramics[J].Journal of the European Ceramic Society,2010,30(2):413.
[8]DOSLER U,KRZMANC M M,SUVOROV D.Phase evolution and microwave dielectric properties of MgO-B2O3-SiO2-based glass-ceramics[J].Ceramics International,2012,38(2):1019-1025.
[9]QASRAWI A F,KAYED T S,MERGEN A,et al.Synthesis and characterization of Mg2B2O5[J].Materials Research Bulletin,2005,40(4):583-589.
[10]WEI J,LIU P,LIN H,et al.Crystal structure and microwave dielectric properties of CaTiO3 modified Mg2Al4Si5O18cordierite ceramics[J].Journal of Alloys and Compounds,2016,689:81-86.
[11]LIOU Y C,WU Y C.Microwave dielectric properties of ZnNb2O6-SrTiO3stacked resonators[J].Journal of Electronic Materials,2017,46(4):2387-2392.
[12]GEORGE S,SEBASTIAN M T.Synthesis and microwave dielectric properties of novel temperature stable high Q,Li2ATi3O8(A=Mg,Zn)ceramics[J].Journal of the American Ceramic Society,2010,93(8):2164.