汽车曲轴用含硫易切削钢C38N2硫化物控制的工艺实践

详细信息    查看全文 | 推荐本文 |

英文篇名：Process Practice of Sulfide Controlling for Free Cutting Steel C38N2 Bearing Sulfur for Auto Crankshaft 作者：郑文超 ; 夏旺苟 ; 何浪 ; 陈国生 ; 张念 英文作者：Zheng Wenchao;Xia Wanggou;He Lang;Chen Guosheng;Zhang Nian;Steel Bar R&D Department,Hubei Xinyegang Steel Co Ltd;Hubei Key Laboratory of High Quality Special Steel,Daye Special Steel Co Ltd;Steelmaking Plant,Hubei Xinyegang Steel Co Ltd; 关键词：含硫易切削钢C38N2 ; MnS ; 钙处理 ; 形态控制 ; 二冷水 ; 结晶器电磁搅拌 英文关键词：Free-Cutting Bearing sulfur Steel C38N2;;MnS;;Calcium Treatment;;Morphology Control;;Secondary Cooling Water;;M-EMS 中文刊名：TSGA 英文刊名：Special Steel 机构：湖北新冶钢有限公司棒材研究所;大冶特殊钢股份有限公司高品质特殊钢湖北重点实验室;湖北新冶钢有限公司炼钢事业部; 出版日期：2019-01-28 出版单位：特殊钢 年：2019 期：v.40;No.225 基金：国家重点研发计划项目资助(2016YFB0300100) 语种：中文; 页：TSGA201901014 页数：4 CN：01 ISSN：42-1243/TF 分类号：49-52

摘要

C38N2钢(/%:0. 36～0.40C,0. 50～0.65Si,1. 40～1. 55Mn,≤0. 025P,0. 010～0.040S,0.10～0.25Cr,≤0.01Al,0. 015～0.020N)的生产工艺流程为120 t BOF-LF-RH-410 mm×530 mm连铸坯-连轧成Φ170 mm材。统计分析了精炼渣碱度(2. 0～5. 5)、成品钢中Ca含量(0～0. 075%)、中间包覆盖剂碱度(5. 94和1. 70)、二冷水(0. 14～0. 24 L/kg)和结晶器搅拌电流(250 A和100 A)对钢中硫化物的影响,通过采用2～3低碱度精炼渣,控制[Ca]/[S]>0. 03,使用1.70碱度中间包覆盖剂,二冷水0.24 L/kg,结晶器搅拌电流100 A等工艺措施,使钢中A类细系硫化物≤2.5级的比率从工艺改进前80%提高至95%,钢中小尺寸、弥散分布的球形或纺锤形硫化物明显增多。
        The production process flowsheet of steel C38 N2(/% : 0. 36 ～0.40 C,0. 50 ～0. 65 Si,1.40 ～1. 55 Mn,≤0.025 P, 0.010 ～0.040 S, 0. 10 ～0.25 Cr, ≤0.01 Al, 0.015 ～ 0.020 N) is 120 t-BOF-LF-RH-410 mm x 530 mm bloom casting-continuous rolling to Φ170 mm products. The statistics of effect of refining slag basicity(2. 0 ～ 2. 5), Ca content in finished steel(0 ～0. 075%),tundish shielding agent basicity(5. 94 and 1. 70), secondary cooling water(0.14 ～0. 24 L/kg) and mould electromagnetic stirring current(250 A and 100 A) on sulfide in steel has been analyzed.With process measures including using 2 ～3 low basicity slag.in refining, controlling [Ca]/[S] >0. 03, using tundish shielding agent basicity 1. 70, secondary cooling water rate 0. 24 L/kg and mould electromagnetic stirring current 100 A,the ratio of rating ≤2. 5 of A-thin series sulfide in steel increases from 80% before process improvement to 95%, and the fine, dispersed distributed spheroidal and spindle-shaped sulfide in steel increases markedly.

引文

[1]李润霞,顾文涛,胡喜军.含硫齿轮钢夹杂物控制[C]. 2012年全国炼钢-连铸生产技术会论文集,重庆:2012:439-445.
    [2] Brunet J C,Torerat P, Hugo M, et al. Influence Des Inclusions De Sulfures Sur Le Comportement a La Rupture Des Aciers De Construction Metallique[J]. Rev Metall, 1977,27(1):1-3.
    [3]张海霞,梁娜,翟正龙,等.易切削钢中硫化物形态的研究[J].冶金丛刊,2011,196(6):8-11.
    [4]代刚,朱志红,储晓明.易切削钢cf53硫含量控制工艺设计与实践[J].特钢技术,2014,79(2):12-14.
    [5]常开地,陈明跃,张慧封,等.转炉生产含硫非调质钢中硫化物夹杂的研究[C].2004年中国金属学会青年学术年会论文集,福州:2004.
    [6]袁婷,李国忠,周兴海,等.Ca-Si处理对易切削非调质钢30MnVS中硫化物形态和成分的影响[J].特殊钢,2009,30(5):39-41.
    [7]杨文,杨小刚,张立峰,等.钢中MnS夹杂物控制综述[J].炼钢,2013,29(6):71-78.
    [8]卢献忠,吴润,吴海涛,等.钢中硫化物的形成及作用进展[J].材料导报,2010,24(7):81-84.
    [9]吴华杰,岳峰,尤大利,等.Mn/S对含硫非调质钢中硫化物形态的影响[J].北京科技大学学报,2014,36(1):50-52.
    [10]郭登仰,吴晓东,陈瑞泷,等.钙处理含硫20CrMo齿轮钢夹杂物析出研究[J].钢铁钒钛,2012,33(6):69-73.