本文对冶炼Fe Mo62钼铁的单位炉料热效应进行了试验,试验结果表明:最佳热效应为2 379.76 k J/kg炉料,且在配料时添加石灰,能够确保冶炼试验顺利进行,生产工艺可控,质量稳定,钼的回收率相应较高。
The thermal effect of Fe Mo62 molybdenum iron smelting was tested. The results show that its best heat effect was 2379. 76 k J/kg furnace charge,and lime adding could ensure the smooth operation of the smelting test,controllable smelting production process,stable quality,higher molybdenum recovery rate.