Producing of 415 ton ingot for backup roll in the conditions of PJSC《Energomashspetsstal》

详细信息    查看全文 | 下载全文 | 推荐本文 |

• 作者：EFIMOV MaximRYABTSEV AnatoliySELYUTIN OlexandrTROYANSKYY OlexandrYAVTUSHENKO Pavel
• 会议时间：2013-06-01
• 关键词：ingot ; 415 ton ; technology ; melting ; pouring ; casting ; rollers ; non-metallic inclusions
• 作者单位：EFIMOV Maxim,SELYUTIN Olexandr,YAVTUSHENKO Pavel(PJSC《 Energomashspetsstal》,Kramatorsk 84306,Ukraine)RYABTSEV Anatoliy,TROYANSKYY Olexandr(State High Educational Institution《 Donetsk National Technical University》,Donetsk 83001,Ukraine)
• 母体文献：第五届宝钢学术年会论文集
• 会议名称：第五届宝钢学术年会
• 会议地点：上海
• 主办单位：中国金属学会
• 语种：chi

摘要

Results of work on melting,pouring,forging and heat treatment of 415 ton ingots from steel of 45 H3 MIF as semiproducts for manufacturing of large backup rolls according to order of company《 Severstal》 are described.For the production of rollers new grade of steel on a base 0.45% C and 3% Cr,alloyed additionally by Mo and V is developed on PJSC《 Energomashspetsstal》 and applied in industry.Steel of bainite class,provides the best combination of strength and plasticity properties.Preparation of metal was produced by melting of the 7 heats in arc steel-melting furnaces with the capacity 100 and 50 tons with subsequent out-of-furnace treatment on ladle- furnace and ladle-degassing units.The pouring of steel was carried out from four steel-pouring ladles in vertical mould under a vacuum through a tundish ladle with protection of stream by argon.Forging of ingots was conducted on the automated forging complex by force of 150 MN.Obtained billets exposed to primary heat treatment,which consisting in heating for recrystallization,isothermal soaking,to providing the removal of residual stresses,additional dehydrogenization,giving to material the lower hardness and controlled cooling for prevention of snowflake formation.Heating of ingots for forging and preliminary heat treatment was carried out in heat treatment furnaces with carrying capacity t0 500 ton.For heat treatment of backup roll horizontal sprayer unit was applied.Tooling of backup roll was executed on a lathe with one pace-plate and final mechanical treatment conducted on the machine-tool of Hercules NWD 1 500 × 18 000 CNC.Finished products with mass of 225 ton of the followings sizes:a diameter and length of barrel 2 360 mm and 4 800 mm accordingly at general length 10 650 mm were obtained.