Study on Corrosion Property of Fluoride Treated Biodegradable AZ31 Magnesium Alloy

详细信息    查看全文 | 下载全文 | 推荐本文 |

• 作者：ZHANG Chun-yanLIU Xin-pengYE Hong
• 会议时间：2014-04-21
• 关键词：Magnesium alloys ; Corrosion ; Surface treatment ; Biomaterials
• 作者单位：College of Materials Science & Engineering, Chongqing University of Technology Chongqing 400054, China
• 母体文献：2014(重庆)国际表面工程论坛暨第十二届全国表面工程·电镀与精饰年会论文集
• 会议名称：2014(重庆)国际表面工程论坛暨第十二届全国表面工程·电镀与精饰年会
• 会议地点：重庆
• 主办单位：中国表面工程协会
• 语种：chi

摘要

In order to improve the corrosion resistance of Mg alloys as degradable implant material, fluorine conversion coatings were synthesized on AZ31 magnesium alloy by immersion in hydrofluoric acid (HF) for different time.Potential dynamic electrochemical technique and hydrogen evolution testing were employed to investigate the corrosion behavior of the coated alloys in Hank's solution.It is indicated that the fluoride conversion coating, which is compact and composed of MgF2, can significantly decrease the degradation rate of Mg alloy AZ31 in Hank's solution.The most improved corrosion protection was achieved by immersion for 10 days.The corrosion current density was 40 times lower than that of the substrate and.the hydrogen evolution rate of the coated sample was only one-fiftieth of the substrate.