Non lead based ternary solid solution 72.5(Bi1/2Na1/2TiO3)–22.5(Bi1/2K1/2TiO3)–5(BiMg1/2Ti1/2O3) with high piezoelectric coefficient (d33) of 180 pC/N has been prepared. Further, magnetoelectric (ME) particulate composites (1 − x)[72.5(BNT)-22.5(BKT)-5(BMgT)] − x CoFe2O4 (CFO) (x = 0, 0.1, 0.2, 0.3) were synthesized and a systematic study of structural, ferroelectric, magnetic and ME properties was undertaken. Large ME voltage coefficient (αE) values accompanied by large piezoelectric coefficient and the adequate interface contact between the magnetic and electric phases were observed in these composites. The composite with x = 0.2, showed the large value of ME voltage coefficient (αE) ~112 mV/cmOe due to higher d33 (~125 pC/N) of composite. The present study demonstrate a new environmental-friendly ME particulate composite for future applications.