Warm-white persistent luminescence of Lu₃Al₂Ga₃O₁₂:Pr³⁺ phosphor

详细信息    查看全文

• 作者：Lin FENG (冯 琳) ; Zhenbin WANG (王振斌) ; Cheng CAO (曹 程) ; Teng ZHANG (张 腾) ; Jiachi ZHANG (张加驰) ; ^{zhangjch@lzu.edu.cn} ; Zhipeng CI (慈志鹏) ; ^{cizhp@lzu.edu.cn} ; Zhengyan ZHAO (赵争妍) ; Yuhua WANG (王育华)
• 关键词：persistent luminescence ; Lu3Al2Ga3O12 ; Pr3+ ; phosphor ; rare earths
• 刊名：Journal of Rare Earths
• 出版年：2017
• 出版时间：January 2017
• 年：2017
• 卷：35
• 期：1
• 页码：47-52
• 全文大小：3306 K
• 卷排序：35

文摘

A warm-white emitting persistent luminescence phosphor Lu3Al2Ga3O12:Pr3+ was synthesized by solid state method at 1600 °C in air. The refined crystal structure of Lu3Al2Ga3O12 host was solved by X-ray diffraction (XRD). The photoluminescence spectra, decay curve and thermoluminescence were investigated. It was revealed that the persistent luminescence originated from the f-f transitions of Pr3+ emitters at Lu3+ sites in LuO8 polyhedrons, and it showed white color due to the 3P0→3H4, 3P1→3H5, 3P0→3H5, 3P0→3H6, 3P0→3F2, 3P0→3F3 and 3P0→3F4 transitions of Pr3+ emitters in a wide range. The persistent luminescence of Pr3+ in this host could be promoted by f-d transition (278 nm) but f-f transitions, due to the different thermal activation energy. The persistent luminescence of the optimal sample could be actually recorded for 3 h by the definition of 0.32 mcd/m2 and was visible for more than 7 h by dark-adapted vision in darkness. The initial depth of the dominant shallow traps was calculated to be about 0.56 eV, which is suitable for persistent luminescence. The different roles of the shallow and deep traps on the persistent decay process were investigated. Accordingly, the persistent luminescence processes and mechanism of the as-synthesized Lu3Al2Ga3O12:Pr3+ phosphors were proposed.