化学成分对球团矿抗压强度影响的研究现状
|
摘要
综述了不同化学成分对球团矿抗压强度的影响。结果发现:球团矿抗压强度的获得主要由赤铁矿晶粒的互连晶决定,改变球团矿的化学成分,球团矿中矿物组成和赤铁矿晶粒间的连晶程度发生改变,进而使球团矿的抗压强度受到影响。本文加深了对球团矿抗压强度获得的认识,可为通过配矿来提高球团矿的强度提供其理论基础。
The effect of chemical composition on the compressive strength of pellets were reviewed. The results show that,the compressive strength of the pellets was mainly determined by the hematite interconnect-crystal grains. The mineral composition and the crystallization degree of hematite crystal of pellets will be change with the change of the chemical composition of pellets,then the compressive strength of pellets is affected. In this paper,the understanding of the obtaining compressive strength of the pellets is profounder,and it could provides theoretical basis to improve the strength of the pellets by ore matching.
The effect of chemical composition on the compressive strength of pellets were reviewed. The results show that,the compressive strength of the pellets was mainly determined by the hematite interconnect-crystal grains. The mineral composition and the crystallization degree of hematite crystal of pellets will be change with the change of the chemical composition of pellets,then the compressive strength of pellets is affected. In this paper,the understanding of the obtaining compressive strength of the pellets is profounder,and it could provides theoretical basis to improve the strength of the pellets by ore matching.
引文
[1]谢路奔.含镁球团焙烧固结强化及其机理研究[D].长沙:中南大学,2012.
[2]许满兴,张玉兰.新世纪我国球团矿生产技术现状及发展趋势[J].烧结球团,2017,42(2):25-30.
[3]杨晓东,张丁辰,刘锟,等.球团替代烧结——铁前节能低碳污染减排的重要途径[J].工程研究——跨学科视野中的工程,2017,9(1):44-52.
[4]朱德庆,潘建.改善球团性能的“碱”与“镁”——碱度和Mg O含量对镜铁矿球团强度及还原行为的影响[N].中国冶金报,2015-12-24(1-3).
[5]王钢,田军,姚燕,等.球团矿抗压强度指标对含粉率及高炉生产的影响分析[J].甘肃冶金,2014,154(6):35-37.
[6]卓凤荣,段再基.提高回转窑球团矿抗压强度的实践[J].山东工业技术,2016(15):236-237.
[7]陈耀明,张元波.氧化球团矿结晶规律的研究[J].钢铁研究,2005,33(3):10-12.
[8]张亚平,傅菊英,江涛,等.脉石含量对球团矿性能的影响[J].烧结球团,2002,27(4):11-14.
[9]王筱留.钢铁冶金学(炼铁部分)[M].北京:冶金工业出版社(第二版),2011.
[10]傅菊英,王黎光,汤曙光,等.不同Si O2源对酸性球团结构和性能的影响[J].钢铁研究,2001,1(3):1-5.
[11]蔡幸福,田铁磊.碱度对高镁碱性球团强度的影响[J].矿产综合利用,2014(4):48-51.
[12]蒋大军,林千谷,何木光,等.不同碱度与配矿结构对球团矿性能的影响[J].四川冶金,2009,31(5):7-11.
[13]杨杰康,王福才,王星富,等.提高钒钛球团矿碱度试验[J].云南冶金,2013,42(6):50-56.
[14]周明顺,沈峰满,翟立委,等.Mg O添加方式对改善球团矿冶金性能的影响[J].钢铁,2012,47(4):14-18.
[15]刘超,张玉柱,康月,等.Mg O含量对低硅烧结成矿性能的影响[J].铸造技术,2017,38(4):885-888
[16]龙跃,徐晨光,张彦辉,等.Mg O对高镁碱性球团矿强度的影响[J].钢铁钒钛,2016,37(4):99-104.
[17]高强健,魏国,何奕波,等.Mg O对球团矿抗压强度的影响[J].东北大学学报(自然科学版),2013,34(1):103-106.
[18]李杰,韩闯闯,杨爱民,等.Mg O含量对镁质熔剂性球团性能的影响[J].烧结球团,2017,42(2):31-37.
[19]潘建,于鸿宾,朱德庆,等.Mg O含量及来源对磁铁精矿球团固结行为的影响[J].中南大学学报(自然科学版),2016,47(9):2914-2920.
[20]赵庆杰,王常任.硼铁矿的开发利用[J].辽宁化工,2001(7):297-299.
[21]程功金,薛向欣程,姜涛,等.B2O3对高铬型钒钛磁铁矿球团抗压强度的影响[C]//第十届中国钢铁年会暨第六届宝钢学术年会论文集II,上海:2015:1-4.
[22]张凯,杨兆祥.添加硼铁精矿对球团矿抗压强度和还原性的影响[J].烧结球团,1998(3):25-28.
[23]高强健,魏国,姜鑫,等.添加硼泥对球团强度影响[J].材料与冶金学报,2013,12(1):1-3.
[24]陈露露.我国钒钛磁铁矿资源利用现状[J].中国资源综合利用,2015,33(10):31-33.
[25]唐珏,张勇,储满生,等.高铬型钒钛磁铁矿配量增加对氧化球团质量的影响[J].东北大学学报(自然科学版),2013,34(7):956-960.
[26]王勇,王涛.8 m2竖炉钒钛球团矿生产实践[J].甘肃冶金,2011,33(1):10-13.
[2]许满兴,张玉兰.新世纪我国球团矿生产技术现状及发展趋势[J].烧结球团,2017,42(2):25-30.
[3]杨晓东,张丁辰,刘锟,等.球团替代烧结——铁前节能低碳污染减排的重要途径[J].工程研究——跨学科视野中的工程,2017,9(1):44-52.
[4]朱德庆,潘建.改善球团性能的“碱”与“镁”——碱度和Mg O含量对镜铁矿球团强度及还原行为的影响[N].中国冶金报,2015-12-24(1-3).
[5]王钢,田军,姚燕,等.球团矿抗压强度指标对含粉率及高炉生产的影响分析[J].甘肃冶金,2014,154(6):35-37.
[6]卓凤荣,段再基.提高回转窑球团矿抗压强度的实践[J].山东工业技术,2016(15):236-237.
[7]陈耀明,张元波.氧化球团矿结晶规律的研究[J].钢铁研究,2005,33(3):10-12.
[8]张亚平,傅菊英,江涛,等.脉石含量对球团矿性能的影响[J].烧结球团,2002,27(4):11-14.
[9]王筱留.钢铁冶金学(炼铁部分)[M].北京:冶金工业出版社(第二版),2011.
[10]傅菊英,王黎光,汤曙光,等.不同Si O2源对酸性球团结构和性能的影响[J].钢铁研究,2001,1(3):1-5.
[11]蔡幸福,田铁磊.碱度对高镁碱性球团强度的影响[J].矿产综合利用,2014(4):48-51.
[12]蒋大军,林千谷,何木光,等.不同碱度与配矿结构对球团矿性能的影响[J].四川冶金,2009,31(5):7-11.
[13]杨杰康,王福才,王星富,等.提高钒钛球团矿碱度试验[J].云南冶金,2013,42(6):50-56.
[14]周明顺,沈峰满,翟立委,等.Mg O添加方式对改善球团矿冶金性能的影响[J].钢铁,2012,47(4):14-18.
[15]刘超,张玉柱,康月,等.Mg O含量对低硅烧结成矿性能的影响[J].铸造技术,2017,38(4):885-888
[16]龙跃,徐晨光,张彦辉,等.Mg O对高镁碱性球团矿强度的影响[J].钢铁钒钛,2016,37(4):99-104.
[17]高强健,魏国,何奕波,等.Mg O对球团矿抗压强度的影响[J].东北大学学报(自然科学版),2013,34(1):103-106.
[18]李杰,韩闯闯,杨爱民,等.Mg O含量对镁质熔剂性球团性能的影响[J].烧结球团,2017,42(2):31-37.
[19]潘建,于鸿宾,朱德庆,等.Mg O含量及来源对磁铁精矿球团固结行为的影响[J].中南大学学报(自然科学版),2016,47(9):2914-2920.
[20]赵庆杰,王常任.硼铁矿的开发利用[J].辽宁化工,2001(7):297-299.
[21]程功金,薛向欣程,姜涛,等.B2O3对高铬型钒钛磁铁矿球团抗压强度的影响[C]//第十届中国钢铁年会暨第六届宝钢学术年会论文集II,上海:2015:1-4.
[22]张凯,杨兆祥.添加硼铁精矿对球团矿抗压强度和还原性的影响[J].烧结球团,1998(3):25-28.
[23]高强健,魏国,姜鑫,等.添加硼泥对球团强度影响[J].材料与冶金学报,2013,12(1):1-3.
[24]陈露露.我国钒钛磁铁矿资源利用现状[J].中国资源综合利用,2015,33(10):31-33.
[25]唐珏,张勇,储满生,等.高铬型钒钛磁铁矿配量增加对氧化球团质量的影响[J].东北大学学报(自然科学版),2013,34(7):956-960.
[26]王勇,王涛.8 m2竖炉钒钛球团矿生产实践[J].甘肃冶金,2011,33(1):10-13.