水玻璃发泡保温材料的制备
详细信息 查看官网全文
- 英文论文题名：Preparation of sodium silicate foam insulation material
- 论文作者：崔荣 ; 徐泽丰 ; 金江 ; 张华
- 英文论文作者：Cui Rong ; Xu Zefeng ; Jin Jiang ; Zhang Hua ; School of Materials Science and Engineering ; Nanjing University of Technology
- 年：2016
- 作者机构：南京工业大学材料科学与工程学院;
- 论文关键词：水玻璃 ; 保温材料 ; 抗压强度 ; 憎水性
- 英文论文关键词：sodium silicate ; insulation material ; compressive strength ; hydrophobicity
- 会议召开时间：2016-11-14
- 会议录名称：2016年全国无机硅化物行业年会暨创新发展研讨会论文集
- 语种：中文
- 分类号：TU551
- 学会代码：WJYG
- 会议名称：2016年全国无机硅化物行业年会暨创新发展研讨会
- 会议地点：中国河南郑州
- 主办单位：中国无机盐工业协会无机硅化物分会
- 学会名称：中国无机盐工业协会无机硅化物分会
- 页数：5
- 文件大小：915k
- 原文格式：O
- 会议级别：全国
摘要
以钠水玻璃为主要原料,制备得到具有良好隔热效果的无机轻质发泡保温材料。利用TGDSC确定加热温度,扫描电镜表征材料的微孔结构。研究了粉煤灰、氯化铝及有机硅对材料性能的影响,通过添加粉煤灰和氯化铝提高材料的抗压强度,加入憎水剂提高材料的憎水性。实验表明:水玻璃中添加12%(质量分数)的粉煤灰,4.5%(质量分数)的氯化铝和0.8%(质量分数)的有机硅,加热温度为250℃,制备出的保温材料抗压强度为0.81 MPa,接触角为159°,材料在100℃下保温10 h的收缩率为1.91%。
The inorganic lightweight foam materials with excellent thermal insulation were prepared using sodium silicate as main raw materials.The heating temperature was determined by TG-DSC.The microporous structure of foaming material was characterized by scanning electron microscope.The influence of fly ash,aluminum chloride,and silicone on the properties of the material was studied.Compressive strength was improved by the addition of the fly ash and aluminum chloride.The hydro-phobicity was enhanced by adding silicone.The lightweight sodium silicate foam insulator with additive of 12%(mass fraction,same below) fly ash,4.5%aluminum chloride,and 0.8%silicone was prepared by controlling the heating temperature at 250 ℃.The prepared inorganic lightweight foam materials showed enhanced compressive strength of 0.81 MPa,better hydrophobicity with contact angle of 159°,and lower shrinkage percentage of 1.91%at 100℃ for 10 h.
The inorganic lightweight foam materials with excellent thermal insulation were prepared using sodium silicate as main raw materials.The heating temperature was determined by TG-DSC.The microporous structure of foaming material was characterized by scanning electron microscope.The influence of fly ash,aluminum chloride,and silicone on the properties of the material was studied.Compressive strength was improved by the addition of the fly ash and aluminum chloride.The hydro-phobicity was enhanced by adding silicone.The lightweight sodium silicate foam insulator with additive of 12%(mass fraction,same below) fly ash,4.5%aluminum chloride,and 0.8%silicone was prepared by controlling the heating temperature at 250 ℃.The prepared inorganic lightweight foam materials showed enhanced compressive strength of 0.81 MPa,better hydrophobicity with contact angle of 159°,and lower shrinkage percentage of 1.91%at 100℃ for 10 h.
引文