对采用焦亚硫酸钠/空气法处理含氰电镀废水进行了试验研究。结果表明,在pH为10.0,焦亚硫酸钠投加量为CN-质量的7.5倍,曝气量为300 L/min的条件下,处理60 min后的废水中总氰化物浓度低于0.3mg/L,具有较好的除氰效果。
This article gives a description of treating electroplating wastewater containing cyanide by Na_2S_2O_5/Air method. The research results showed that,under the optimal condition that,the pH value was 10,the ratio of Na_2S_2O_5 to CN-was 7.5 to 1,the air provision was 300 L/min,the reaction time was 60 minutes,a desirable result was achieved that the cyanide mass concentration of treated electroplating wastewater containing cyanide was decreased to 0.3mg/L.