Li_2CO_3对高钛型高炉渣提钛后急冷渣水化性能的影响
|
摘要
利用等离子熔融技术提取硅钛合金后的急冷尾渣制备铝酸钙水泥。用化学结合水法、孔径分布、XRD以及SEM分析手段,研究Li2CO3对提钛后急冷残渣水化性能的影响。结果表明:提钛后急冷尾渣主要由玻璃相和部分一铝酸钙(CA)以及镁铝尖晶石(MA)组成,具有一定的水化性能;加入Li2CO3能明显促进急冷渣水化,增强急冷渣砂浆强度,提高水化后孔隙率和初期的结合水量,但Li2CO3加入量不应超过0.1%。
The rapid cooling tailings produced in the process of silicon-titanium alloy extraction from high titanium blast furnace slags by plasma fusion technique were used as raw materials to prepare calcium aluminate cement.The chemically combined water content analysis,pore size distribution test,XRD and SEM were employed to investigate the effect of Li2CO3 on the hydration properties of the tailings.The results show that the rapid cooling tailings,mainly consisting of glass phase and also containing part of calcium aluminate(CA) and magnesia alumina spinel(MA) phases,have weak hydration ability;hydration of the tailings can be significantly promoted,and the mortar strength,porosity after hydration and bounding water in early hydration of the tailings are increased by adding not more than 0.1% Li2CO3.
The rapid cooling tailings produced in the process of silicon-titanium alloy extraction from high titanium blast furnace slags by plasma fusion technique were used as raw materials to prepare calcium aluminate cement.The chemically combined water content analysis,pore size distribution test,XRD and SEM were employed to investigate the effect of Li2CO3 on the hydration properties of the tailings.The results show that the rapid cooling tailings,mainly consisting of glass phase and also containing part of calcium aluminate(CA) and magnesia alumina spinel(MA) phases,have weak hydration ability;hydration of the tailings can be significantly promoted,and the mortar strength,porosity after hydration and bounding water in early hydration of the tailings are increased by adding not more than 0.1% Li2CO3.
引文
[1]Li Youqi,Ke Changming,Hou Shixi,et al.Smelting reduction research of induction furnace on Panzhihua Iron and Steel CO.BF slag containing titanium[J].Refractory,2007,41(Supplement):244-247.(李有奇,柯昌明,侯世喜,等.攀钢含钛高炉渣的感应炉熔融还原研究[J].耐火材料,2007,41(增刊):244-247.)
[2]Wang Peng,Han Bingqiang,Han Yanlei,et al.Research on hydration capability of Panzhihua Iron and Steel Co.BF slag after extracting silicon-titanium alloy[J].Bulletin of Chinese Ceramic Society,2008,27(6):1208-1230.(汪朋,韩兵强,韩彦雷,等.攀钢高炉渣提钛后尾渣水化性能研究[J].硅酸盐通报,2008,27(6):1208-1230.)
[3]Wang Peng,Han Bingqiang,Ke Changming,et al.Research on properties of corundum castables bonded by Panzhihua Iron and Steel Co.BF slag after extracting silicon-titanium alloy[J].Journal of Wuhan University of Science and Technology(Natural Science Edition),2008,31(Supplement):120-122.(汪朋,韩兵强,柯昌明,等.攀钢高炉提钛尾渣结合刚玉浇注料性能研究[J].武汉科技大学学报(自然科学版),2008,31(增刊):120-122.)
[4]Shi Jinhui,Xiao Guoqing.Effect of additives on bongding strength of the new spinel-containing aluminous cements[J].Bulletin of Chinese Ceramic Society,2009,28(1):176-179.(石金辉,肖国庆.外加剂对含镁铝尖晶石新型铝酸盐水泥结合强度的影响[J].硅酸盐通报,2009,28(1):176-179.)
[5]Yuan Runzhang.Gelling material science.[M].Wuhan:Wuhan University of Science and Technology Press,2003:188-190.(袁润章.胶凝材料学[M].武汉:武汉理工大学出版社,2003:188-190.)
[6]Yang Nanru.The physical and chemical basis of alkali cementitious materials(Ⅰ)[J].Journal of Silicate,1996,24(2):209-215.)(杨南如.碱胶凝材料的物理化学基础(Ⅰ)[J].硅酸盐学报,1996,24(2):209-215.)
[7]Yang Nanru.The physical and chemical basis of alkali cementitious materials(Ⅱ)[J].Journal of Silicate,1996,24(4):459-465.)(杨南如.碱胶凝材料的物理化学基础(Ⅱ)[J].硅酸盐学报,1996,24(4):459-465.)
[2]Wang Peng,Han Bingqiang,Han Yanlei,et al.Research on hydration capability of Panzhihua Iron and Steel Co.BF slag after extracting silicon-titanium alloy[J].Bulletin of Chinese Ceramic Society,2008,27(6):1208-1230.(汪朋,韩兵强,韩彦雷,等.攀钢高炉渣提钛后尾渣水化性能研究[J].硅酸盐通报,2008,27(6):1208-1230.)
[3]Wang Peng,Han Bingqiang,Ke Changming,et al.Research on properties of corundum castables bonded by Panzhihua Iron and Steel Co.BF slag after extracting silicon-titanium alloy[J].Journal of Wuhan University of Science and Technology(Natural Science Edition),2008,31(Supplement):120-122.(汪朋,韩兵强,柯昌明,等.攀钢高炉提钛尾渣结合刚玉浇注料性能研究[J].武汉科技大学学报(自然科学版),2008,31(增刊):120-122.)
[4]Shi Jinhui,Xiao Guoqing.Effect of additives on bongding strength of the new spinel-containing aluminous cements[J].Bulletin of Chinese Ceramic Society,2009,28(1):176-179.(石金辉,肖国庆.外加剂对含镁铝尖晶石新型铝酸盐水泥结合强度的影响[J].硅酸盐通报,2009,28(1):176-179.)
[5]Yuan Runzhang.Gelling material science.[M].Wuhan:Wuhan University of Science and Technology Press,2003:188-190.(袁润章.胶凝材料学[M].武汉:武汉理工大学出版社,2003:188-190.)
[6]Yang Nanru.The physical and chemical basis of alkali cementitious materials(Ⅰ)[J].Journal of Silicate,1996,24(2):209-215.)(杨南如.碱胶凝材料的物理化学基础(Ⅰ)[J].硅酸盐学报,1996,24(2):209-215.)
[7]Yang Nanru.The physical and chemical basis of alkali cementitious materials(Ⅱ)[J].Journal of Silicate,1996,24(4):459-465.)(杨南如.碱胶凝材料的物理化学基础(Ⅱ)[J].硅酸盐学报,1996,24(4):459-465.)