考虑相差异的煤矿液压支柱缸体用27SiMn钢组织性能预测
|
摘要
利用JMatPro软件模拟了液压支柱缸体用27SiMn钢凝固和冷却过程的组织与性能。计算时,考虑不同相的组织性能差异,得到室温至熔化温度区间合金中主要相的热物理性能参数和部分力学性能参数,以及27SiMn钢冷却过程的CCT曲线。结果表明:27SiMn钢奥氏体转变温度区间为716~838℃;在900~1453℃,存在MNS相;在1414~1468℃,奥氏体含量开始减小,高温铁素体相增大。当温度低于731.64℃时,有渗碳体析出;当温度低于380℃时,有M7C3形成,室温平衡组织为铁素体+渗碳体+M3P+M7C3。
The microstructure and properties of hydraulic prop cylinder used 27SiMn steel in process of solidification and cooling was simulated.In calculation,considering the difference of different phase's microstructure and properties,the thermal physical performance parameters and some mechanical properties for the main phase from room temperature to the melting temperature,as well as the CCT curve were obtained.The results show that:the transition temperature range for austenite is 716-838 ℃;MNS phase exists at 900-1453℃,At 1414-1468 ℃,the austenite content begins to decrease and high-temperature ferrite phase increases.In addition,when the temperature is lower than 731.64℃,the cementite precipitates;and M7C3 appears when the temperature is below 380 ℃,the final room temperature equilibrium microstructure is ferrite,cementite,M3P and M7C3.
The microstructure and properties of hydraulic prop cylinder used 27SiMn steel in process of solidification and cooling was simulated.In calculation,considering the difference of different phase's microstructure and properties,the thermal physical performance parameters and some mechanical properties for the main phase from room temperature to the melting temperature,as well as the CCT curve were obtained.The results show that:the transition temperature range for austenite is 716-838 ℃;MNS phase exists at 900-1453℃,At 1414-1468 ℃,the austenite content begins to decrease and high-temperature ferrite phase increases.In addition,when the temperature is lower than 731.64℃,the cementite precipitates;and M7C3 appears when the temperature is below 380 ℃,the final room temperature equilibrium microstructure is ferrite,cementite,M3P and M7C3.
引文
[1]任鑫,张若愚,杜学芸,等.27SiMn钢化学镀Ni-P和Ni-Ce-P性能对比研究[J].热加工工艺,2012,41(8):147-149.
[2]任鑫,王世臣,王万鹏,等.27SiMn钢化学镀Ni-P一纳米A1203研究[J].热加工工艺.2010,39(24):152-154.
[3]李安铭,李小飞,陈昊.27SiMn钢奥氏体逆相变亚温淬火[J].煤炭学报,2008,33(9):1063-1066.
[4]张太超,彭竹琴.27SiMn钢临界温度淬火高温回火后的力学性能[J].金属热处理,2003,28(10):32-34.
[5]李智丽,杨维宇,白雅琼,等.27SiMn钢奥氏体连续冷却转变曲线[J].热加工工艺,2011,40(22):45-47.
[6]杜晗婷,陈冰泉,牟军伟,等.轧辊堆焊温度场的动态有限元模拟[J].电焊机,2007,37(11):44-48.
[7]李晓峰,陈冰泉,黄永溪.JMatPro软件在药芯焊丝W110性能研究中的应用[J].热加工工艺,2010,39(9):5-7.
[8]闵永安,刘湘江,毛远建.应用JMatPro软件对比研究两种抽油杆钢的合金化特点[J].上海大学学报:自然科学版,2008,14(5):503-508.
[2]任鑫,王世臣,王万鹏,等.27SiMn钢化学镀Ni-P一纳米A1203研究[J].热加工工艺.2010,39(24):152-154.
[3]李安铭,李小飞,陈昊.27SiMn钢奥氏体逆相变亚温淬火[J].煤炭学报,2008,33(9):1063-1066.
[4]张太超,彭竹琴.27SiMn钢临界温度淬火高温回火后的力学性能[J].金属热处理,2003,28(10):32-34.
[5]李智丽,杨维宇,白雅琼,等.27SiMn钢奥氏体连续冷却转变曲线[J].热加工工艺,2011,40(22):45-47.
[6]杜晗婷,陈冰泉,牟军伟,等.轧辊堆焊温度场的动态有限元模拟[J].电焊机,2007,37(11):44-48.
[7]李晓峰,陈冰泉,黄永溪.JMatPro软件在药芯焊丝W110性能研究中的应用[J].热加工工艺,2010,39(9):5-7.
[8]闵永安,刘湘江,毛远建.应用JMatPro软件对比研究两种抽油杆钢的合金化特点[J].上海大学学报:自然科学版,2008,14(5):503-508.