摘要
彩色氧化锆陶瓷的制备方法主要有:固相混合法、化学共沉淀法、液相浸渗法、高温渗碳法等。本文详细介绍了固相混合法,化学共沉淀法和液相浸渗法的工艺原理,分析比较了各种制备工艺的优缺点,并且对这几种制备工艺的研究进展进行了综述。
The preparation methods of colored zirconia ceramics include solid phase mixing, chemical co-precipitation, liquid phase infiltration, high temperature carbonization and so on. This paper introduced in detail the principles of these methods, compared their advantages and disadvantages, and reviewed their research progress.
引文
[1]谢志鹏.结构陶瓷[M].北京:清华大学出版社,2010.
[2]张永胜,胡丽天,陈建敏.氧化锆纳米陶瓷素坯成型研究[J].材料热处理学报,2005,26(6):5-8.ZHANG Y S,HU L T,CHEN J M.Transactions of Materials and Heat Treatment,2005,26(6):5-8.
[3]ETOH S,ARAHORI T,MORI K,et al.Machinable ceramic of blackish color used in probe guides comprises solid particles of boron nitride,zirconia and silicon nitride,sintering aid and coloring additive:US,2005130829-A1[P].2004-09-17.
[4]BRIOD R.Method of manufacturing a black zirconia-based article and black zirconia-based decorative article notably obtained by this method:US,5711906-A[P].1995-04-17.
[5]刘丽菲.高韧性彩色氧化锆陶瓷的制备及性能研究[D].吉林:吉林大学,2009:29-60.
[6]张灿英,朱海涛,李长江.彩色氧化锆陶瓷的制备[J].稀有金属材料与工程,2007,36:266-268.ZHANG C Y,ZHU H T,LI C J.Rare Metal Materials and Engineering,2007,36:266-268.
[7]FENG R,NOBUYUKI T.Color and vanadium valency in V-doped zirconia[J].J Am Ceram Soc,1993,76:1825-1832.
[8]李懋强.湿化学法合成陶瓷粉料的原理和方法[J].硅酸盐学报,1994,22(1):85-91.LI M Q.Journal of the Chinese Ceramic Society,1994,22(1):85-91.
[9]徐跃萍,郭景坤,黄校先,等.无团聚氧化锆-Y2O3陶瓷超细粉的制备及微观结构表征[J].硅酸盐学报,1991,19(6):269-273.XU Y P,GUO J K,HUANG X X,et al.Journal of the Chinese Ceramic Society,1991,19(6):269-273.
[10]FUJISAKI H,HIROYUKI F.Zirconia-containing powder for black zirconia sintered body,e.g.for ornamental articles such as watch bands,contains specified amount of cobalt-zinc-ironaluminum or aluminum oxide containing pigment,aluminum oxide,and yttrium oxide:JP,2007308338-A[P].2006-05-18.
[11]千粉玲,谢志鹏,孙家林,等.非均匀沉淀法制备黑色氧化锆陶瓷[J].硅酸盐学报,2011,39(9):1290-1294.QIAN F L,XIE Z P,SUN J L,et al.Journal of the Chinese Ceramic Society,2011,39(9):1290-1294.
[12]TU W C,LANGE F F.Liquid precursor infiltration processing of powder compacts.1.Kinetic studies and microstructure development[J].J Am Ceram Soc,1995,78:3277-3282.
[13]MARPLE B R,GREEN D J.Mullite alumina particulate composites by infiltration processing[J].J Am Ceram Soc,1989,72:2043-2048.
[14]MARPLE B R,GREEN D J.Graded compositions and microstructures by infiltration processing[J].Journal of Materials Science,1993,28:4637-4643.
[15]张丽莉,谢志鹏,刘伟,等.氧化锆陶瓷注射成型溶剂脱脂行为的研究[J].陶瓷学报,2011,32(04):501-505.ZHANG L L,XIE Z P,LIU W,et al.Solvent debinding behavior of zirconia powder injection molding[J].Journal of Ceramics,2011,32(04):501-505.
[16]FISCHER H,WEISS R,TELLE R.Crack healing in alumina bioceramics[J].Dental Materials,2008,24:328-332.
[17]DARBY R J,FARNAN I,KUMAR R V.Method for making minor dopant additions to porous ceramics[J].Advances in Applied Ceramics,2009,108:506-508.
[18]LIU G W,XIE Z P,WANG W,et al.Fabrication of coloured zirconia ceramics by infiltrating water debound injection moulded green body[J].Advances in Applied Ceramics,2011,110:58-62.
[19]ZHONG W,YU L,LI H.A synthesis method of black zirconia:CN,1566021A[P].2005-04-13.
[20]B·米歇尔.获得有金色金属外观的氧化锆基制品的方法.中国.1179921C[P].2004-12-15.
[21]B·米歇尔.着色氧化锆制品的生产方法和获得的着色氧化锆装饰制品.中国.1241551A[P].2000-01-19.