The deuterium depth distribution for a 20 keV/D D_3~+beam implanted into ytterbium(Yb) at a temperature between 300 and 340 K was studied using the D(d,p)T reaction.By analyzing the proton yields,the deuterium depth distribution from the front surface to 500 nm depth was found.The results indicate that an equilibrium deuterium distribution region from the front surface to a depth approximately equal to the mean range of implanted deuterons was formed in Yb during the implantation.The deduced deuterium concentration in the equilibrium deuterium distribution region was D/Yb = 22%.
The deuterium depth distribution for a 20 keV/D D_3~+beam implanted into ytterbium(Yb) at a temperature between 300 and 340 K was studied using the D(d,p)T reaction.By analyzing the proton yields,the deuterium depth distribution from the front surface to 500 nm depth was found.The results indicate that an equilibrium deuterium distribution region from the front surface to a depth approximately equal to the mean range of implanted deuterons was formed in Yb during the implantation.The deduced deuterium concentration in the equilibrium deuterium distribution region was D/Yb = 22%.
引文
1 P.G.Shewmon,Diffusion in solids(New York:Mc Graw-Hill,1963)
2 J.R.Manning,Diffusion kinetics for atoms in crystals(New York:D.V.Nostrand,1968)
3 C.M.Bartle et al,Nucl.Instrum Methods,95:221-228(1971)
4 P.B.Johnson,Nucl.Instrum Methods,114:467-475(1974)
5 A.E.Pontau et al,J.Nucl.Mater.,91:343-346(1980)
6 Y.Takeuchi et al,J.Appl.Phys.,64:2959-2963(1988)
7 S.M.Myers et al,Phys.Rev.B,43:9503-9510(1991)
8 H.Kudo et al,J.Nucl.Mater.,258-263:622-627(1998)
9 Z.Qin et al,J.Nucl.Mater.,264:228-233(1999)
10 N.Kawachi et al,Nucl.Instrum Methods B,190:195-198(2002)
11 V.Kh.Alimov et al,J.Nucl.Mater.,337-339:619-623(2005)
12 D.J.Cherniak et al,Chem.Geol.,268(1):155-166(2009)
13 W.R.Wampler et al,J.Nucl.Mater.,415(1):S653-656(2011)
14 J.T.Zhao et al,Nucl.Instrum.Methods B,316:13-16(2013)
15 H.Yuki et al,J.Phys.Soc.Jpn.,66:73-78(1997)
16 K.H.Fang et al,J.Phys.Soc.Jpn.,80:084201(2011)
17 J.T.Zhao,Ph.D.thesis(Lanzhou University,2013)
18 J.T.Zhao et al,Nucl.Instrum Methods B,299:54-60(2013)
19 H.Yuki et al,J.Phys.G:Nucl.Part.Phys.,23:1459-1464(1997)
20 H.Y.Lv et al,Chinese Phys.C,35:26-30(2011)
21 H.J.Assenbaum et al,Z.Phys.A,327:461-468(1987)
22 S.Engstler et al,Phys.Lett.B,202:179-184(1988)
23 T.S.Wang et al,J.Phys.G:Nucl.Part.Phys.,39:015201(2012)
24 L.Bracci et al,Nucl.Phys.A,513:316-343(1990)
25 C.Kittel,Introduction to Solid State Physics(New York:John Wiley&Sons,Inc.,1986)
26 T.S.Wang et al,Nucl.Instrum Methods B,269:2721-2725(2011)
27 F.Raiola et al,Eur.Phys.J.A,13:377-382(2002)
28 J.F.Ziegler,J.P.Biersack,code SRIM(http://www.srim.org)
29 F.Raiola,Ph.D.thesis(Ruhr-Universit¨at Bochum,2005)
30 M.B.Lewis,J.Nucl.Mater.,88:23-30(1980)
31 S.T.Picraux,F.L.Vook,Radiation Effects,11:179-192(1971)
32 V.Kh.Alimov et al,J.Nucl.Mater.,241-243:1047-1052(1997)