Q355NHD耐候H型钢生产实践
|
摘要
基于耐候钢生产技术难点,详细分析论述了首钢长治钢铁公司Q355NHD耐候H型钢的生产工序、加热工序、轧制工序和检测方法。检测表明:成品钢材表面无裂纹,化学成分、力学性能等指标满足国家标准,表现出优良的耐大气腐蚀性能,是一种具有广阔前景的绿色钢材。基于生产实践基础上的改造,可推广至其它耐候钢生产过程。
The production process, heating process, rolling process and inspection method of Q355NHD weathering H-steel by Shougang Changzhi Iron & Steel Co., Ltd. are described in detail based on the production technological difficulties of weathering steel. Inspection shows that, the surface of finished steel has no crack, and indexes such as chemical composition as well as mechanical properties meet the national standard, showing excellent resistance to atmospheric corrosion, being a kind of eco-friendly steel with broad prospect. On the basis of such a production practice, it can also be extended to other weathering steel production process.
The production process, heating process, rolling process and inspection method of Q355NHD weathering H-steel by Shougang Changzhi Iron & Steel Co., Ltd. are described in detail based on the production technological difficulties of weathering steel. Inspection shows that, the surface of finished steel has no crack, and indexes such as chemical composition as well as mechanical properties meet the national standard, showing excellent resistance to atmospheric corrosion, being a kind of eco-friendly steel with broad prospect. On the basis of such a production practice, it can also be extended to other weathering steel production process.
引文
[1]谢世红,汪开忠,吴结才,等.铁道车辆用耐候H型钢的开发[J].钢铁研究,2005,33(1):25-27.
[2]王振波.钢结构建筑防腐技术[J].工程设计与研究,2012(2):26-27.
[3]谢世红.马钢开发耐候H型钢的可行性分析[C]//中国金属学会青年学术年会.2002.
[4]刘炳宇,刘昆华.转炉-连铸工艺生产重轨钢的实践[C]//全国炼钢学术会议.2002:9-12.
[5]李率民,胥克宝,万友堂,等.耐候钢板表面微裂纹研究[J].宽厚板,2009,15(3):15-17.
[2]王振波.钢结构建筑防腐技术[J].工程设计与研究,2012(2):26-27.
[3]谢世红.马钢开发耐候H型钢的可行性分析[C]//中国金属学会青年学术年会.2002.
[4]刘炳宇,刘昆华.转炉-连铸工艺生产重轨钢的实践[C]//全国炼钢学术会议.2002:9-12.
[5]李率民,胥克宝,万友堂,等.耐候钢板表面微裂纹研究[J].宽厚板,2009,15(3):15-17.