基于图书馆背景的苯丙乳液改性研究
|
摘要
苯丙乳液(苯乙烯-丙烯酸酯乳液)通过的是苯乙烯、丙烯酸酯单体经乳液共聚得到的,其在耐水性、耐碱性、耐洗擦等方面有了一定的应用。通过反应性乳化剂、苯乙烯(ST)、甲基丙烯酸等进行了改性处理,实验采用种子滴加法得到共聚物乳液。实验结果表明:改性的苯丙乳液满足了技术要求,其耐水性能优越;随着引发剂用量的增加,单体的转化率上升,凝聚率上升;乳化剂用量为4.5%,聚合稳定性最好;在最佳配比2∶5时,更能发挥两类乳化剂的协同效应。
Styrene acrylic emulsion is always prepared by the emulsion copolymerization of styrene and acrylate monomer. Because of good water resistance, alkali resistance and scrub resistance, it has a certain application value. In this paper, the copolymer emulsion was obtained by the modification with reactive emulsifier, styrene(ST) and methacrylate. The experimental results showed that the modified styrene acrylic emulsion met the technical requirements and had superior water resistance. With the increase of the initiator dosage, the conversion rate of monomer increased and the condensation rate increased. When the dosage of emulsifier was 4.5%, the polymerization stability was the best. The synergistic effect of two types of emulsifiers was enhanced when the optimum ratio was 2.5.
Styrene acrylic emulsion is always prepared by the emulsion copolymerization of styrene and acrylate monomer. Because of good water resistance, alkali resistance and scrub resistance, it has a certain application value. In this paper, the copolymer emulsion was obtained by the modification with reactive emulsifier, styrene(ST) and methacrylate. The experimental results showed that the modified styrene acrylic emulsion met the technical requirements and had superior water resistance. With the increase of the initiator dosage, the conversion rate of monomer increased and the condensation rate increased. When the dosage of emulsifier was 4.5%, the polymerization stability was the best. The synergistic effect of two types of emulsifiers was enhanced when the optimum ratio was 2.5.
引文
[1]夏伟.苯丙乳液改性的研究与应用进展[J].当代化工研究,2018(03):141-142.
[2]司景航,许孟杰,周雪松.油水分离滤纸的制备及其性能研究[J/OL].中国造纸:1-7[2018-06-13].http://kns.cnki.net/kcms/detail/11.1967.TS.2018 0522.1606.004.html.
[3]邢小光,许金余,白二雷,王谕贤.苯丙乳液改性砂浆的优化配比及其性能研究[J].硅酸盐通报,2018,37(04):1174-1180.
[4]陈中华,梁家妮.以负载缓蚀剂的二氧化硅微胶囊制备水性智能防腐涂料及其涂层性能研究[J].电镀与涂饰,2018,37(06):231-235.
[5]白龙,王勇,马小龙,霍月青,牛金平.双烷基二苯醚双磺酸钠的合成及其在乳液聚合中的应用[J].印染助剂,2018,35(03):16-20+49.
[6]刘博,杨扬,李萍,詹予忠.纸质文物用功能型苯丙乳液施胶剂的合成研究[J].中国胶粘剂,2018,27(02):35-38.
[7]张恒,张守杰,郝新宇.聚合物改性硅粉混凝土力学性能研究[J].水利科学与寒区工程,2018,1(02):9-13.
[8]唐兵,龚博文,赵凯.重涂底漆苯丙乳液的制备[J].中国涂料,2018,33(02):25-29.
[9]孟亚飞,汪滨,王娇娜,裴广玲.苯丙乳液的成膜性能与静电纺丝工艺研究[J].膜科学与技术,2018,38(01):44-50+60.
[10]李鹏.聚合物改性再生骨料透水砖的性能研究[J].新型建筑材料,2018,45(02):137-140.
[11]施秀琴,姚浩伟,晏建波,代培刚,梁栋.防火型建筑水性无机涂料的研制[J].消防科学与技术,2018,37(02):235-237.
[12]邓爱民,赵闯,穆锐.端丙烯酸基二代超支化聚酯的合成及其在苯丙乳液中的应用研究[J].沈阳理工大学学报,2018,37(01):28-32+38.
[13]刘德红,刘芝君,王振,张逸超,李之锋.树脂基料对超薄型钢结构防火涂料性能的影响[J].新型建筑材料,2018,45(01):37-39+66.
[14]王露,陈王觅,衣守志.纳米隔热保温涂料的制备与性能研究[J].现代化工,2018,38(04):165-168.
[15]廖桥,李碧雄,吴瑾炎,彭博.基于力学性能的秸秆纤维混凝土配合比试验研究[J].混凝土世界,2018(01):84-88.
[16]王健雁,刘萍,唐爱东,潘春跃.聚合物乳液对发泡水泥板的改性研究[J].湖南工业大学学报,2017,31(06):72-77.
[17]张兴,乔永洛,申亮.塑胶漆用苯丙乳液制备及漆膜性能研究[J].江西科技师范大学学报,2017(06):55-59.
[18]司景航,梁家丽,周雪松.阳离子型苯丙乳液的合成与应用[J].造纸科学与技术,2017,36(06):52-56+60.
[19]杨光,邓安仲.添加纳米二氧化硅对苯丙涂层综合性能的影响[J].材料保护,2017,50(12):1-4+58.
[20]左艳梅.半连续种子乳液预聚法合成核-壳型苯丙乳液的研究进展[J].中国胶粘剂,2017,26(11):39-44.
[21]杨光,邓安仲.棕色反射隔热外墙涂层的制备及性能[J].电镀与涂饰,2017,36(22):1178-1182.
[22]方永勤,王瑾,许亮.APS-AIBN引发体系对苯丙乳液聚合过程及涂层性能的影响[J].常州大学学报(自然科学版),2017,29(06):8-14.
[23]颜朝霞,郭勇,马和平,张晓娜.新型环保水性带锈防锈涂料的研制[J].甘肃科技纵横,2017,46(11):22-24+17.
[24]李依芮,曾晓辉,冉宇舟,梁坤,王平.地铁用绝缘水泥基材料试验研究[J].铁道建筑,2017,57(11):141-144.
[25]肖玮.探索复合型保温隔热涂料的制备与研发[J].居舍,2017(31):22.
[26]林杰生,李广彦,张心亚.纤维增强型聚合物水泥防水浆料的制备与性能[J].涂料技术与文摘,2017,38(10):36-42+46.
[27]王梓旭,裴世红,赵月.改性核/壳型苯丙乳液及油水分离性能[J].现代化工,2017,37(12):139-142+144.
[28]沈怡甜.碳纳米管对苯丙乳液防火涂料的抑烟性能[J].消防科学与技术,2017,36(10):1428-1430.
[29]周婕,陈来,王坤,汪承磊.高阻尼性涂层用苯丙乳液的制备与性能研究[J].涂料工业,2017,47(10):23-28.
[30]杨光,邓安仲.光谱选择性散热涂层的制备及性能[J].电镀与涂饰,2017,36(18):961-965.
[31]杨光,邓安仲.面漆对镍钛黄建筑节能涂层性能的影响[J].电镀与涂饰,2017,36(18):966-970.
[32]李丹琳,晏建波,代培刚,关健玲,李冬敏.透明防火型水性无机涂料的研制及防火性能评价[J].广东化工,2017,44(18):40-41.
[33]杨光,邓安仲.涂层结构对建筑节能涂层性能的影响[J].表面技术,2017,46(09):48-53.
[34]彭光,许金余,任韦波.聚合物水泥路面填缝材料变形性能研究[J].硅酸盐通报,2017,36(09):2894-2899.
[35]赵月,裴世红,王梓旭.有机硅氧烷改性St/BA/AA三元共聚乳液的制备[J].合成化学,2017,25(10):836-839.
[36]贺晓宇.氯丁乳液与苯丙乳液掺量对水泥砂浆性能的影响研究[J].路基工程,2017(04):136-140.
[37]杨光,邓安仲,陈静波.KH560改性纳米硅溶胶对苯丙涂层性能的影响[J].表面技术,2017,46(08):49-54.
[38]朱从进,白二雷,许金余,聂良学.灰粉比对苯丙乳液基水泥复合填缝料剪切性能的影响[J].硅酸盐通报,2017,36(08):2576-2582.
[39]杜武青,毕静仪,李敏,刘英炎,黄志勇,林楚宏.苯丙乳液基膨胀型阻燃涂料的配方研究[J].中国安全科学学报,2017,27(08):38-43.
[40]杨光,邓安仲,王友军.纳米二氧化硅对苯丙乳液涂层力学性能的影响[J].后勤工程学院学报,2017,33(04):58-63.
[2]司景航,许孟杰,周雪松.油水分离滤纸的制备及其性能研究[J/OL].中国造纸:1-7[2018-06-13].http://kns.cnki.net/kcms/detail/11.1967.TS.2018 0522.1606.004.html.
[3]邢小光,许金余,白二雷,王谕贤.苯丙乳液改性砂浆的优化配比及其性能研究[J].硅酸盐通报,2018,37(04):1174-1180.
[4]陈中华,梁家妮.以负载缓蚀剂的二氧化硅微胶囊制备水性智能防腐涂料及其涂层性能研究[J].电镀与涂饰,2018,37(06):231-235.
[5]白龙,王勇,马小龙,霍月青,牛金平.双烷基二苯醚双磺酸钠的合成及其在乳液聚合中的应用[J].印染助剂,2018,35(03):16-20+49.
[6]刘博,杨扬,李萍,詹予忠.纸质文物用功能型苯丙乳液施胶剂的合成研究[J].中国胶粘剂,2018,27(02):35-38.
[7]张恒,张守杰,郝新宇.聚合物改性硅粉混凝土力学性能研究[J].水利科学与寒区工程,2018,1(02):9-13.
[8]唐兵,龚博文,赵凯.重涂底漆苯丙乳液的制备[J].中国涂料,2018,33(02):25-29.
[9]孟亚飞,汪滨,王娇娜,裴广玲.苯丙乳液的成膜性能与静电纺丝工艺研究[J].膜科学与技术,2018,38(01):44-50+60.
[10]李鹏.聚合物改性再生骨料透水砖的性能研究[J].新型建筑材料,2018,45(02):137-140.
[11]施秀琴,姚浩伟,晏建波,代培刚,梁栋.防火型建筑水性无机涂料的研制[J].消防科学与技术,2018,37(02):235-237.
[12]邓爱民,赵闯,穆锐.端丙烯酸基二代超支化聚酯的合成及其在苯丙乳液中的应用研究[J].沈阳理工大学学报,2018,37(01):28-32+38.
[13]刘德红,刘芝君,王振,张逸超,李之锋.树脂基料对超薄型钢结构防火涂料性能的影响[J].新型建筑材料,2018,45(01):37-39+66.
[14]王露,陈王觅,衣守志.纳米隔热保温涂料的制备与性能研究[J].现代化工,2018,38(04):165-168.
[15]廖桥,李碧雄,吴瑾炎,彭博.基于力学性能的秸秆纤维混凝土配合比试验研究[J].混凝土世界,2018(01):84-88.
[16]王健雁,刘萍,唐爱东,潘春跃.聚合物乳液对发泡水泥板的改性研究[J].湖南工业大学学报,2017,31(06):72-77.
[17]张兴,乔永洛,申亮.塑胶漆用苯丙乳液制备及漆膜性能研究[J].江西科技师范大学学报,2017(06):55-59.
[18]司景航,梁家丽,周雪松.阳离子型苯丙乳液的合成与应用[J].造纸科学与技术,2017,36(06):52-56+60.
[19]杨光,邓安仲.添加纳米二氧化硅对苯丙涂层综合性能的影响[J].材料保护,2017,50(12):1-4+58.
[20]左艳梅.半连续种子乳液预聚法合成核-壳型苯丙乳液的研究进展[J].中国胶粘剂,2017,26(11):39-44.
[21]杨光,邓安仲.棕色反射隔热外墙涂层的制备及性能[J].电镀与涂饰,2017,36(22):1178-1182.
[22]方永勤,王瑾,许亮.APS-AIBN引发体系对苯丙乳液聚合过程及涂层性能的影响[J].常州大学学报(自然科学版),2017,29(06):8-14.
[23]颜朝霞,郭勇,马和平,张晓娜.新型环保水性带锈防锈涂料的研制[J].甘肃科技纵横,2017,46(11):22-24+17.
[24]李依芮,曾晓辉,冉宇舟,梁坤,王平.地铁用绝缘水泥基材料试验研究[J].铁道建筑,2017,57(11):141-144.
[25]肖玮.探索复合型保温隔热涂料的制备与研发[J].居舍,2017(31):22.
[26]林杰生,李广彦,张心亚.纤维增强型聚合物水泥防水浆料的制备与性能[J].涂料技术与文摘,2017,38(10):36-42+46.
[27]王梓旭,裴世红,赵月.改性核/壳型苯丙乳液及油水分离性能[J].现代化工,2017,37(12):139-142+144.
[28]沈怡甜.碳纳米管对苯丙乳液防火涂料的抑烟性能[J].消防科学与技术,2017,36(10):1428-1430.
[29]周婕,陈来,王坤,汪承磊.高阻尼性涂层用苯丙乳液的制备与性能研究[J].涂料工业,2017,47(10):23-28.
[30]杨光,邓安仲.光谱选择性散热涂层的制备及性能[J].电镀与涂饰,2017,36(18):961-965.
[31]杨光,邓安仲.面漆对镍钛黄建筑节能涂层性能的影响[J].电镀与涂饰,2017,36(18):966-970.
[32]李丹琳,晏建波,代培刚,关健玲,李冬敏.透明防火型水性无机涂料的研制及防火性能评价[J].广东化工,2017,44(18):40-41.
[33]杨光,邓安仲.涂层结构对建筑节能涂层性能的影响[J].表面技术,2017,46(09):48-53.
[34]彭光,许金余,任韦波.聚合物水泥路面填缝材料变形性能研究[J].硅酸盐通报,2017,36(09):2894-2899.
[35]赵月,裴世红,王梓旭.有机硅氧烷改性St/BA/AA三元共聚乳液的制备[J].合成化学,2017,25(10):836-839.
[36]贺晓宇.氯丁乳液与苯丙乳液掺量对水泥砂浆性能的影响研究[J].路基工程,2017(04):136-140.
[37]杨光,邓安仲,陈静波.KH560改性纳米硅溶胶对苯丙涂层性能的影响[J].表面技术,2017,46(08):49-54.
[38]朱从进,白二雷,许金余,聂良学.灰粉比对苯丙乳液基水泥复合填缝料剪切性能的影响[J].硅酸盐通报,2017,36(08):2576-2582.
[39]杜武青,毕静仪,李敏,刘英炎,黄志勇,林楚宏.苯丙乳液基膨胀型阻燃涂料的配方研究[J].中国安全科学学报,2017,27(08):38-43.
[40]杨光,邓安仲,王友军.纳米二氧化硅对苯丙乳液涂层力学性能的影响[J].后勤工程学院学报,2017,33(04):58-63.
© 2004-2018 中国地质图书馆版权所有 京ICP备05064691号 京公网安备11010802017129号 地址：北京市海淀区学院路29号 邮编：100083 电话：办公室：(+86 10)66554848；文献借阅、咨询服务、科技查新：66554700 |