采用模板法将纳米二氧化钛粒子负载于氨基化的交联聚苯乙烯微球表面,再经过高温煅烧,最终得到一种具有多孔结构的空心二氧化钛微球。并研究了该空心二氧化钛作为光催化剂降解罗丹明的性能,结果表明该催化剂具有较好的光催化活性。
The hollow titanium dioxide microspheres with porous structure was fabricated in a process by nanometer titanium dioxide particles were coating on the surface of the aminated crosslinked polystyrene microspheres followed by calcining at high temperature by the template method. and The degradation performance of rhodamine was studied by using the hollow titanium dioxide as photocatalyst. The results showed that the catalyst had good photocatalytic activity.
引文
[1]刘立华,张瑞.处理染料废水的研究进展[J].化工科技市场,2005,28(1):20-23.
[2]李伟,侯楚楚,毛子文,等.光催化降解甲基橙过程的评价方法研究[J].浙江外国语学院学报,2011(4):28-36.
[3]徐守斌,江龙,朱云峰,等.染料废水的光催化处理[J].化工进展,2009,28(1):428.
[4]胡冬娜,田秀君.具有可见光活性催化剂的研究现状及应用进展[J].山西建筑,2006,32(24):174-175.
[5]Bai B,Wang P P,Wu L,et al.A novel yeast bio-template route to synthesize Cr2O3hollow microspheres[J].Mater Chem Phys,2009,114(1):26-28.
[6]Liu Z Y,Sun D D,Guo P.One-step fabrication and high photocatalytic activity of porous Ti O2hollow aggregates by using a low-temperature hydrothermal method without templates[J].Chem Eur J,2007,13(6):1851-1858.
[7]Zhang Y F,Feng X H,Liu H,et al.Self-assembly Ti O2hierarchical hollow microspheres with rutile nanorods by template-free hydrothermal method[J].Chem Lett,2008,37:1624-1630.
[8]Lee S H A,Abrams N M,Hoertz P G.Coupling of titania inverse opals to nanocrystalline titania layers in dye-sensitized solar cells[J].J Phys Chem B,2008,112(46):14415-14421.
[9]Jeong U,Im S H,Camargo P H C.Microscale fish bowls:a new class of latex particles with hollow interiors and engineered porous structures in their surfaces[J].Langmuir,2007,23(22):10968-10975.
[10]Naganine S,Sugioka A,Konishi Y.Preparation of Ti O2hollow microparticles by spraying water droplets into an organic solution of titanium tetraisopropoxide[J].Mater Lett,2007,61(2):444-451.
[11]裴爱华,杨桂生,沈征武.模板法制备无机氧化物中空微球的研究进展[J].高分子通报,2005(2):1-7.
[12]Kim T H,Lee K H,Kwon Y K.Monodisperse hollow titania nanosphers prepared using a cationic colloidal template[J].Journal of Colloid and Interface Science,2006,304:370-377.
[13]Yoon S B,Kim J Y,Kim J H,et al.Template synthesis of nanostructureed silica with hollow core and mesoporous shell structures[J].Current Applied Physics,2006(6):1059-1063.
[14]Chen M,Wu L M,Zhou S X,et al.A method for the fabrication of monodisperse hollow silica spheres[J].Adv Mater,2006,18:801-803.
[15]Caruso R A,Susha A,Caruso F.Multilayered titania,silica and laponite nanoparticle coating on polystyrene colloidal templates and resulting inorganic hollow spheres[J].Chemistry of Materials,2001,13:400-409.
[16]Caruso F,Caruso R A,Moehwald H.Nanoengineering of inorganic and hybrid hollow spheres by colloidal templating[J].Science,1998,282(20):1111-1114.
[17]Zhou J,Chen M,Qiao X.Facile preparation method of Si O2/PS/Ti O2multilayer core-shell hybrid microspheres[J].Langmuir,2006,22(12):10175-10179.
[18]Choi W S,Koob H Y,Huck W T S.Synthesis of raspberrylike particles using polyelectrolyte multilayer-coated particles[J].Mater Chem,2007,17(47):4943-4946.
[19]罗祖云,冯振亮,洪若瑜.二氧化钛空心微球的制备及在光催化降解有机色素方面的应用[J].福建师范大学福清分校学报,2016(2):27-31.