Single-crystallize phase Li-伪-Sialon with equiaxial morphology has been successfully synthesized by solid state reaction at 1700 掳C for 1 h under a N2 atmosphere. The effects of additions SiO2 and Al2O3, holding time at 1050 掳C and packing powders, on the phase compositions and Li contents of products have been investigated by XRD, SEM, EDS and ICP-OES. The results showed that additions SiO2 and Al2O3, holding time at 1050 掳C and packing powders played an important role in retarding the vaporization of lithium and forming Li-伪-Sialon, where the former two ways were by formation of more Li-containing liquid while the latter was by providing a source of Li-containing vapor and increasing partial pressure of Li in the surrounding gaseous environment resulting in preventing volatilization of Li from the sample. However, there were more or less AlN, AlSi0.5O2.5, 尾-Sialon present in the products when these factors were ignored.