Enhancement of the Hydrogen Evolution Reaction from Ni-MoS2 Hybrid Nanoclusters

详细信息    查看全文

• 作者：Daniel Escalera-López ; Yubiao Niu ; Jinlong Yin ; Kevin Cooke ; Neil V. Rees ; Richard E. Palmer
• 刊名：ACS Catalysis
• 出版年：2016
• 出版时间：September 2, 2016
• 年：2016
• 卷：6
• 期：9
• 页码：6008-6017
• 全文大小：635K
• 年卷期：0
• ISSN：2155-5435

文摘

This report focuses on a novel strategy for the preparation of transition metal–MoS₂ hybrid nanoclusters based on a one-step, dual-target magnetron sputtering, and gas condensation process demonstrated for Ni-MoS₂. Aberration-corrected STEM images coupled with EDX analysis confirms the presence of Ni and MoS₂ in the hybrid nanoclusters (average diameter = 5.0 nm, Mo:S ratio = 1:1.8 ± 0.1). The Ni-MoS₂ nanoclusters display a 100 mV shift in the hydrogen evolution reaction (HER) onset potential and an almost 3-fold increase in exchange current density compared with the undoped MoS₂ nanoclusters, the latter effect in agreement with reported DFT calculations. This activity is only reached after air exposure of the Ni-MoS₂ hybrid nanoclusters, suggested by XPS measurements to originate from a Ni dopant atoms oxidation state conversion from metallic to 2+ characteristic of the NiO species active to the HER. Anodic stripping voltammetry (ASV) experiments on the Ni-MoS₂ hybrid nanoclusters confirm the presence of Ni-doped edge sites and reveal distinctive electrochemical features associated with both doped Mo-edge and doped S-edge sites which correlate with both their thermodynamic stability and relative abundance.