Opening and Closing of Nanocavities under Cyclic Loading in a Soft Nanocomposite Probed by Real-Time Small-Angle X-ray Scattering
详细信息 查看全文
- 作者：Huan Zhang ; Arthur K. Scholz ; Fabien Vion-Loisel ; Yannick Merckel ; Mathias Brieu ; Hugh Brown ; St茅phane Roux ; Edward J. Kramer ; Costantino Creton
- 刊名：Macromolecules
- 出版年：2013
- 出版时间：February 12, 2013
- 年：2013
- 卷：46
- 期：3
- 页码：900-913
- 全文大小：687K
- 年卷期：v.46,no.3(February 12, 2013)
- ISSN：1520-5835
文摘
The opening and closing of nanocavities in a model soft nanocomposite subjected to cyclic uniaxial tension were directly studied by real-time small-angle X-ray scattering (SAXS). The volume fraction and average shape of the nanocavities have been detected by a pronounced increase in the scattering invariant Q/Q0 and a detailed analysis of the scattering patterns. Cavities appear upon loading past an intrinsic stress 蟽int or intrinsic elongation 位int. Upon unloading, nanocavities are progressively closed until the volume void fraction void reaches 0 for a constant 鈥渃losure stress鈥?of about 3.5 MPa. As the sample is reloaded, no cavities are observed when the current elongation remains below the maximum elongation of previous cycles 位max(N 鈥?1) (N is the number of the cycles). Above this elongation, the void volume fraction void of the sample increases again. In contrast with void, the cumulative void volume fraction cum_void appearing in the sample to reach a given maximum historical elongation, 位max, or equivalently maximum historical stress 蟽max, was found to be independent of loading history. Both results point toward a process of creation of nanovoids in confined rubber domains that have not previously cavitated rather than to the reopening of the previously created cavities. All critical cavitation parameters display a strong memory effect, mostly captured in this uniaxial test by the maximum historical stress or elongation. The closure stress probably results from the Laplace pressure. A mechanism based on the rearrangement of filler agglomerates by strong shear stress after the emergence of nanocavities is proposed to account for the formation and release of the local geometric confinement and the non-reopening of the previously opened nanovoids upon reloading.