Eu2+ emission is studied in two types of phosphates A3P4O13 and A3(PO4)2 (A=Sr, Ba). Comparative analysis of EVI parameter was done for Barium- and Strontium- based phosphates. Huang-Rhys factor and effective phonon energies shows intermediate coupling of electron-vibration interaction.