Precise small-angle X-ray scattering evaluation of the pore structures in track-etched membranes: Comparison with other convenient evaluation methods

详细信息    查看全文

• 作者：Tsukasa Miyazaki^a ; ^{t_miyazaki@cross.or.jp} ; Mikihito Takenaka^b
• 关键词：Small-angle X-ray scattering ; Track-etched membrane ; Separation property
• 刊名：Nuclear Instruments and Methods in Physics Research Section B: Beam Interactions with Materials and Atoms
• 出版年：2017
• 出版时间：1 March 2017
• 年：2017
• 卷：394
• 期：Complete
• 页码：121-125
• 全文大小：1041 K
• 卷排序：394

文摘

Poly(ethylene terephthalate) (PET)-based track-etched membranes (TMs) with pore sizes ranging from few nanometers to approximately 1 μm are used in various applications in the biological field, and their pore structures are determined by small-angle X-ray scattering (SAXS). These TMs with the nanometer-sized cylindrical pores aligned parallel to the film thickness direction are produced by chemical etching of the track in the PET films irradiated by heavy ions with the sodium hydroxide aqueous solution. It is well known that SAXS allows us to precisely and statistically estimate the pore size and the pore size distribution in the TMs by using the form factor of a cylinder with the extremely long pore length relative to the pore diameter. The results obtained were compared with those estimated with scanning electron microscopy and gas permeability measurements. The result showed that the gas permeability measurement is convenient to evaluate the pore size of TMs within a wide length scale, and the SEM observation is also suited to estimate the pore size, although SEM observation is usually limited above approximately 30 nm.