On the static and dynamic properties of flax and Cordenka epoxy composites

详细信息    查看全文

• 作者：James Meredith^a ; ^{james.meredith@warwick.ac.uk} ; ; Stuart R. Coles^a ; Richard Powe^a ; Ed Collings^b ; Sophie Cozien-Cazuc^c ; Brendon Weager^d ; Jorg Mü ; ssig^e ; Kerry Kirwan^a
• 关键词：A. Structural composites ; B. Impact behaviour ; B. Mechanical properties ; C. Damage mechanics ; D. Optical microscopy
• 刊名：Composites Science and Technology
• 出版年：2013
• 出版时间：17 May, 2013
• 年：2013
• 卷：80
• 期：Complete
• 页码：31-38
• 全文大小：3101 K

文摘

Fibre reinforced composites have excellent specific properties and are widely sought after by engineers seeking to reduce mass. However, end of life disposal is a significant problem and so research into more sustainable natural fibre composites is extremely topical. This paper examines the applicability of natural fibre composites for high performance structural applications. Woven flax and regenerated cellulose (Cordenka) textiles were pre-impregnated with commercially available epoxy resins and consolidated into test laminates in an autoclave to determine their static (compressive, tensile, flexural) and dynamic (energy absorption) properties.

The range of compressive strengths was 77.5-299.6 MPa. Tensile strengths ranged from 63 to 92.6 MPa and interlaminar shear strength (ILSS) from 10.7 to 23.3 MPa. Specific energy absorption (SEA) varied between 21.2-34.2 kJ/kg. Biotex flax combined with MTM49 resin matched the SEA of T300 carbon fibre using the same resin system and layup. This work has demonstrated that natural fibre composites have significant scope for use in structural applications but additional work is required on fibre to matrix bonding in order to maximise their properties whilst remaining an environmentally credible option.